Yes / Polyamide 6 (PA6) is an important engineering thermoplastic, very widely used but prone to thermal degradation during extrusion at temperature not far from its melt temperature (220 oC). Typically, and as measured in this study, PA6 extruded at temperature of 300 oC shows a 40% decrease in tensile modulus compared to non-extruded PA6. To rebuild PA6 molecular weight, the easiest and cheapest method is to use an appropriate chain extender. Many chain extenders have been used in the past but they are essentially suited to nucleophile induced degradation, targeting split PA6 chains carboxyl COOH and amine NH2 end groups. What has been lacking are effective chain extenders for thermally only induced degradation, i.e. for the practical cases where the PA6 is thoroughly dried before extrusion. For such a case, the degradation reaction mechanism dictates that the solution is to develop chain extenders that target the split PA6 chains amide CONH2 groups not the carboxyl COOH and amine NH2 end groups. As amide groups strongly react with anhydride functionalities, we test the effectiveness of a novel chain extender, Joncryl® ADR 3400, a styrene maleic anhydride copolymer with multiple, repeating anhydride functionality. Assessment of chain extension in this study is done as with previous work, using rheology, mechanical and thermal properties of PA6 extruded on its own and with the chain extender. The viscoelastic data conclusively show the efficacy of such chain extender with more than 10 fold changes in the comparative values of the extruded sample storage modulus G' and as much as an 85% increase in the tensile modulus. / Republic of Turkey, Ministry of National Education. University of Bradford
Identifer | oai:union.ndltd.org:BRADFORD/oai:bradscholars.brad.ac.uk:10454/16529 |
Date | 17 October 2018 |
Creators | Tuna, Basak, Benkreira, Hadj |
Source Sets | Bradford Scholars |
Language | English |
Detected Language | English |
Type | Article, Accepted manuscript |
Rights | © 2018 Society of Plastics Engineers. This is the peer reviewed version of the following article: Tuna B and Benkreira H (2019) Reactive extrusion of polyamide 6 using a novel chain extender. Polymer Engineering and Science. 59(s2): E25-E31., which has been published in final form at https://doi.org/10.1002/pen.24944. This article may be used for non-commercial purposes in accordance with Wiley Terms and Conditions for Self-Archiving., Unspecified |
Page generated in 0.0016 seconds