Direct methanol fuel cells (DMFC) are being investigated for use as low-power electrochemical energy conversion devices. These types of fuel cells can be useful for portable electronics. The polymer electrolyte membrane plays a critical role in the overall performance of DMFC. The commercially available membrane, Nafion, suffers from high methanol permeability and a resulting methanol crossover from the anode to the cathode; it is also expensive. Accordingly, alternative membrane materials, such as sulfonated hydrocarbons, are intensively pursued for DMFC. For example, sulfonated poly (ether ether ketone) (SPEEK) and sulfonated polysulfone (SPsf) are two such candidates.
This thesis focuses first on a simple synthesis method for a cross-linked sulfonated polysulfone membrane. Sulfonated polysulfone (Psf) membranes, with high IEC (1.4 - 2.2 meq/g), were characterized by nuclear magnetic resonance spectroscopy (NMR), proton conductivity, and water uptake. The degree of sulfonation was calculated by NMR and verified by acid-base titration analysis. Although the membranes showed good proton conductivity, they suffered from excessive swelling at high temperatures. Furthermore, the post-sulfonation of a carboxyl-substituted polysulfone (Psf-COOH) was carried out with trimethylsilyl chlorosulfonate, and solubility issues of the Psf-COOH in chlorinated solvents led to difficulty in controlling the degree of sulfonation (DS) and in purification. Accordingly, this approach to cross-linking sulfonated polysulfone was rejected as a viable method.
This thesis then focused on the investigation of the mechanical properties of acid-base blend membranes based on SPEEK and heterocycle-tethered Psf and cross-linked membranes based on SPEEK that were previously reported by our group; these membranes were known to exhibit good performance in DMFC. However, the assessment of the mechanical stability of any new membranes developed is critical for their practical viability in DMFC. Accordingly, the mechanical strength and ductility of these membranes were investigated and compared for various membrane compositions. The acid-base blend membranes investigated consisted of SPEEK (acidic polymer) and a heterocycle-tethered Psf (basic polymer); for example, blends consisting of SPEEK and amino-benzimidazole-tethered Psf (SPEEK/Psf-ABIm) and SPEEK and benzotriazole tethered Psf (SPEEK/Psf-Btraz) were investigated. The cross-linked SPEEK was made by Friedel-Craft acylation with Psf-COOH (DS = 1 or 2). The two blend membranes showed superior mechanical properties compared to Nafion 115 and comparable to plain SPEEK. The crosslinked membranes showed good mechanical properties and better strength than Nafion 115, but they were more brittle than both Nafion 115 and plain SPEEK. Further optimization of cross-linking conditions is necessary to produce the best performing membrane. / text
Identifer | oai:union.ndltd.org:UTEXAS/oai:repositories.lib.utexas.edu:2152/ETD-UT-2011-05-3418 |
Date | 08 July 2011 |
Creators | Zieren, Shelley Marie |
Source Sets | University of Texas |
Language | English |
Detected Language | English |
Type | thesis |
Format | application/pdf |
Page generated in 0.0041 seconds