Polymer photovoltaic cell (PV cell) utilizes a polymer to absorb photons for generating excitons. When excitons are separated into electrons and holes, the device has the photovoltaic effect. Polymer light emitting diode (PLED) injects electrons and holes respectively from cathode and anode into a polymer emission layer. Some of the electrons and the holes would recombine to induce light emission.
This research used a heterocyclic aromatic rigid-rod polymer poly-p-phenylene- benzobisoxazole (PBO) as the opto-electronic layer, and a conducting material of poly(3,4-ethylenedioxythiophene):poly(4-styrenesulfonic acid) (PEDOT:PSS) as the hole transport layer. PV cells were fabricated using indium-tin-oxide (ITO) as anode and aluminium as cathode. Same layer arrangement was applied for PLEDs. These two kinds of devices were measured for electrical and optical response.
It was evidenced that the addition of PEDOT:PSS layer facilitated the separation of excitons into electrons and holes at the PBO/PEDOT:PSS interface. Insertion of a LiF layer between PBO layer and Al cathode reduced their energy band gap and facilitated charge transport leading to an enhanced efficiency for PV cells and PLEDs.
Thickness variations were found on spun PBO layer. According to emission intensity, we knew that the PBO layer quality was significant for electroluminescence. Introduction of a PEDOT:PSS layer improved the interface between ITO and PBO. The thickness of PEDOT:PSS layer depended on the ITO surface roughness. With a PEDOT:PSS layer, the opto-electronic efficiency of PV cell and PLED was improved.
Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0724106-193120 |
Date | 24 July 2006 |
Creators | Tsai, Jung-lung |
Contributors | Bae-heng Tseng, Ming Chen, Jui-hung Hsu, Shih-jung Bai |
Publisher | NSYSU |
Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
Language | Cholon |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0724106-193120 |
Rights | not_available, Copyright information available at source archive |
Page generated in 0.0066 seconds