Orientadores: Maria do Carmo Gonçalves, Inez Valeria Pagotto Yoshida / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-10T13:34:02Z (GMT). No. of bitstreams: 1
OliveiraJunior_AdairRangelde_D.pdf: 4693907 bytes, checksum: 00373c55664170beeb525a7a15fd26a8 (MD5)
Previous issue date: 2006 / Resumo: Este trabalho teve como foco principal a obtenção de argilas expandidas por meio da modificação de argila natural com organossilanos, e depois sua incorporação em uma resina de polipropileno em extrusora de rosca dupla para a obtenção de nanocompósitos. As argilas usadas neste estudo foram as argilas montmoriloníticas sódicas Polenita e GelMax, bem como a argila organofílica Viscogel. Os organossilanos empregados no tratamento químico das argilas naturais foram o aminopropiltrimetoxissilano, glicidoxipropiltrietoxissilano e o metacriloxipropiltrietoxissilano. A obtenção da argila expandida foi fortemente influenciada pelas condições reacionais, como tipo e concentração do silano, solvente e pH do meio. As análises de difração de raios X revelaram que os melhores resultados de expansão da argila foram alcançados ao usar o silano aminopropiltrimetoxissilano em meio aquoso na faixa de pH entre 8 e 10. Segundo os dados de análise térmica, esta argila apresentou uma estabilidada térmica bem superior às tradicionais argilas organofílicas. Antes da incorporação da argila à matriz de polipropileno, primeiramente fez-se um estudo de otimização das condições de mistura, usando-se para isto a argila organofílica Viscogel, de elevado espaçamento basal. Desenvolveu-se um perfil de rosca com alta taxa de cisalhamento, no qual foi obtido um nanocompósito com dispersão de tamanho das lamelas da argila entre 5 a 15 nm. Tal dispersão resultou em ganho nas propriedades mecânicas em torno de 30 % em relação ao polipropileno puro. Este perfil de rosca foi, portanto, utilizado para realizar o processamento do polipropileno com a nova argila expandida. A partir dos resultados de difração de raios X e de microscopia eletrônica de transmissão, concluiu-se que não foi possível delaminar totalmente esta argila no polímero, como observado para a argila organofílica. Porém, os resultados relativos às propriedades mecânicas dos materiais obtidos mostraram que a argila modificada com aminopropiltrimetoxis-silano apresentou propriedades semelhantes às da argila organofílica, indicando que apesar do menor grau de dispersão, estas propriedades foram favorecidas pela maior interação entre a argila modificada e a matriz polimérica / Abstract: The purpose of this work was to obtain expanded clay by modifying clay with organosilane, and its incorporation into polypropylene resin to prepare a polypro-pylene-clay nanocomposite. Natural sodium montmorillonite (GelMax, Polenita) as well as organophylic clay (Viscogel ED) were used for this purpose. Three types of silanes were used to modify the clay: Aminopropyltrimethoxysilane (APS), glyci-doxypropyltriethoxysilane (GPS) and methacryloxypropyltrimethoxysilane (MPS). The expanded clay was strongly affected by reaction conditions, such as silane type and concentration, solvent and pH. According to XRD analysis, the higher basal distance was achieved in aqueous dispersion (pH 8-10) using the APS as a modifier. Modified clay showed superior thermal stability in comparison to organo-phylic clay, using thermogravimetric analysis. Besides the clay modification pro-cess, the screw profile influence on nanocomposite properties was also evaluated. An organophylic clay (Viscogel) was used to optimize the extrusion conditions, in this study. The composite processing was carried out in a twin screw extruder with higher shear screw profile. In this way, an exfoliated nanocomposite was obtained, where the clay layer thickness was between 5 and 15 nm. The flexural modulus of such nanocomposite was 30% higher than virgin polypropylene. This higher shear screw profile was used to extrude the polypropylene/aminopropylsilane-modified clay. Based on the X-ray diffraction and transmission electron microscopy results, a satisfactory exfoliation degree for silane-modified clay was not achieved, as observed for organophylic clay. In spite of the low exfoliation level of silane-modi-fied clay, the mechanical properties of its composite were similar to the organo-phylic clay based nanocomposite. This fact was attributed to better adhesion between polypropylene-silane modified clay than the polypropylene-organophylic clay system / Doutorado / Físico-Química / Doutor em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248736 |
| Date | 10 June 2006 |
| Creators | Oliveira Junior, Adair Rangel de |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Yoshida, Inez Valéria Pagotto, 1950-, Gonçalves, Maria do Carmo, 1957-, Mauler, Raquel Santos, Junior, Elias Hage, Nogueira, Ana Flávia, Felisberti, Maria Isabel |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Ciências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 74f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds