Objetivo: Comparar in vitro la fuerza de adhesión de postes de fibra de vidrio tratados con silano en distintos tiempos de evaporación del solvente. Materiales y Métodos: Cuarenta dientes de bovino uniradiculares fueron seccionados separando corona de raíz, obteniendo una raíz remanente de 20mm. Las raíces bovinas fueron tratadas endodónticamente y divididas aleatoriamente en cuatro grupos según el tiempo de evaporación (n=10): G1- 180 segundos; G2- 120 segundos; G3- 60 segundos; G4- Control, sin silanizado. A la superficie del poste se le aplicó el silano ProSil - FGM y se esperó la evaporación del solvente de acuerdo al grupo experimental. Posterior a ello, se cementaron los postes de fibra con el cemento resinoso RelyX U-200TM – 3M ESPE según las instrucciones del fabricante y los especímenes fueron almacenados por 24 horas en agua destilada a 37 oC. Las raíces fueron seccionadas en slides de 1 mm de grosor, utilizando una máquina de corte digital IsoMet® - Low Speed Saw. Para medir la fuerza de adhesión se utilizó el test de push-out en el centro del slide a una velocidad de 0.5 mm/min y medido en KgF/MPa. Resultados: Los valores de fuerza de adhesión según cada grupo fueron: G1- 10.89±2.68; G2-5.50±2.84; G3-2.40±0.89; G4-0.79±0.73. Se comparó la fuerza de adhesión entre los grupos de 60-120s, 120-180s, y 60-180s. Se encontraron diferencias estadísticamente significativas en los tres grupos (p=0.0015, p=0.0015 y p=0.0000 respectivamente). Se comparó entre los tres grupos, encontrándose también diferencias estadísticamente significativas (p=0.0001). Conclusiones: Se encontró que el grupo de 180 segundos de evaporación presentaba una mayor fuerza de adhesión comparada a los demás grupos. / Objective: To compare the fiberglass posts bond strength treated with silane at different solvent evaporation times. Materials and Methods: Forty bovine teeth were seccionated in two, obtaining 20mm bovine roots. Bovine roots were endodontically treated and randomly divided into four groups according to evaporation time (n=10): G1-180 seconds; G2-120 seconds; G3- 60 seconds; G4-control, without silanizing. Prosil – FGM silane was applied to the post surface and was allowed to evaporate according to the time established in the experimental groups. After that, the fiber posts were cemented with RelyX U-200TM – 3M ESPE resin cement according to manufacturer instructions and the samples were stored 24 hours in distilled water at 37 °C. Roots were cut in slides 1 mm thick using a IsoMet® - Low Speed Saw digital cutting machine. Push-out test was used to measure the slide bond strength in KgF/MPa at the speed of 0.5 mm/min. Results: The bond strength values according to each group were: G1-10.89±2.68; G2-5.50±2.84; G3-2.40± 0.89; G4-0.79±0.73. Bond strength was compared between experimental groups 60-120 seconds, 120-180 seconds and 60-180 seconds. Statistically significant differences were found for all three groups (p=0.0015, p=0.0015 and p=0.0000, respectively). Statistically significant differences were also found between the three groups (p=0.0001). Conclusion: The 180 seconds evaporation group showed a higher bond strength compared with the other groups. / Tesis
Identifer | oai:union.ndltd.org:PERUUPC/oai:repositorioacademico.upc.edu.pe:10757/619053 |
Date | 2016 May 1931 |
Creators | Figueroa Yamunaqué, Elena |
Contributors | Revoredo De Rojas, Arturo |
Publisher | Universidad Peruana de Ciencias Aplicadas (UPC), PE |
Source Sets | Universidad Peruana de Ciencias Aplicadas (UPC) |
Language | Spanish |
Detected Language | Spanish |
Type | info:eu-repo/semantics/bachelorThesis |
Format | application/pdf, application/epub, application/msword |
Source | Universidad Peruana de Ciencias Aplicadas (UPC), Repositorio Académico UPC |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds