This thesis describes magnesium alloys, their properties and methods of their production. However, experimental part is focused on AZ91 magnesium alloy. Conversion coatings were prepared on the AZ91 surface – chromate coating, phosphate permanganate coating and fluoride coating. Corrosion resistance of the prepared coatings were compared by immersion tests and by potentiodynamic methods. Evaluation of corrosion resistance by immersion tests was successful only for phosphate permanganate coating. Only this coating was removed during cleaning of the samples. For comparison of corrosion resistance was important to find the correct procedures and optimize the measurements methods. For these purposes have been chosen galvanic zinc coating on steel sheets. Thickness of the zinc coating were 8 and 30 microns. This coatings provide uniform zinc surface without heterogenities which was important for the potentiodynamic measurements. After optimization methods for potentiodynamic measurements by galvanic zinc coatings have been measured magnesium alloy AZ91 uncoated and coated by conversion coatings. For uncoated AZ91 magnesium alloy was determined suitable method so called virgin cathodic curve. On the other hand, for the coated AZ91 magnesium alloys was determined suitable method so called combined curve, within which we measured cyclic voltammetry curve (± 5 mV) and then virgin anodic curve.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:233384 |
| Date | January 2014 |
| Creators | Tkacz, Jakub |
| Contributors | Pacal, Bohumil, Hadzima, Branislav, Havlica, Jaromír |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.002 seconds