Previous issue date: 2014-11-21 / Sem bolsa / Silicone por adição ou polivinilssiloxanos (VPS), são materiais de moldagem elastoméricos caracterizados principalmente pela precisão de impressão, em termos de reprodução de detalhes e precisão dimensional, pré-requisito essencial para uma boa moldagem, e consequentemente uma boa restauração indireta. Assim, o objetivo deste estudo foi avaliar qualitativamente a incorporação de diferentes partículas de reforço em um silicone de adição experimental (VPS) em duas concentrações diferentes, 20% e 40%. O método de depósito foi baseado na adição de partículas de reforço na matriz do polivinilssiloxano para melhorar as propriedades físicas e mecânicas. Para isso, o estudo foi desenvolvido em três fases, que incluem: (i) preparação do polivinilssiloxano experimental; (ii) incorporação de partículas de reforço em diferentes concentrações: a) 20% de partícula de reforço, b) 40% de partículas de reforço; (iii) caracterização do polivinilssiloxano através da análise de resistência à tração, reprodução de detalhes, dureza shore A, recuperação elástica e MEV. Quanto aos resultados obtidos o AE 40% e PAH 40% obtiveram sua habilidade de cópia prejudicada pela alta viscosidade, e apresentaram maior valores de dureza shore A e de resistência a tração. A recuperação elástica não foi estatisticamente significativa. Por conseguinte, características como morfologia, granulometria e quantidade de partículas inorgânicas na matriz polimérica de um polivinilssiloxano são responsáveis pela caracterização das propriedades do material. / Addition silicones or polyvinylsiloxanes are elastomeric impression materials characterized mainly by printing accuracy in terms of detail reproduction and dimensional accuracy, essential pre-requisites for a good impression and consequently a good indirect restoration. So, the aim of the study was to evaluate qualitatively the incorporation of different filler particles on an experimental polyvinylsiloxane (VPS) at two different concentrations, 20% and 40%. An experimental VPS was developed, and on this were deposited different kinds of filler particles. The deposit method was based on adding filler particles onto a VPS matrix to improve physical and mechanical properties. For this, the study was developed in three stages: (i) preparation of an experimental VPS; (ii) filler particle incorporation in different concentrations, (a) 20% filler particle and (b) 40% filler particle; (iii) silicone characterization through analysis of strength tensile, detail reproduction, shore A hardness, elastic recovery and SEM. The results show that AE 40% and PAH 40% had copy ability hampered by high viscosity, and they present the highest shore A hardness and strength tensile values. The elastic recovery was not statistically significant. Therefore, characteristics such as morphology, particle size and amount of filler particles in a VPS matrix are responsible for characterizing the properties of the material.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpel.edu.br:prefix/3455 |
Date | 21 November 2014 |
Creators | Meincke, Débora Könzgen |
Contributors | 97186473091, http://lattes.cnpq.br/5883827704465047, Ogliari, Fabrício Aulo |
Publisher | Universidade Federal de Pelotas, Programa de Pós-Graduação em Odontologia, UFPel, Brasil, Faculdade de Odontologia |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFPEL, instname:Universidade Federal de Pelotas, instacron:UFPEL |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0014 seconds