The aim of this thesis study was to extract nickel and cobalt from Sivrihisar limonitic nickel laterite ore by high pressure acid leaching (HPAL) method under most economical operating parameters. Optimizing the conditions to yield a saleable quality mixed hydroxide product from the pregnant leach solution (PLS) was also investigated.
To extract high amounts of nickel and cobalt from the laterite matrix / leaching duration, leaching temperature and sulfuric acid/ore ratio were studied at fixed conditions of -850 µ / limonitic ore particle size and 40% solids concentration. The Sivrihisar limonitic nickel laterite ore was found to be readily leachable. It was found that 95.4% of Ni and 91.5% of Co were extracted at the optimized conditions of 235oC, 0.23 acid/ore ratio in 60 minutes. The real pregnant leach solution produced at the optimized conditions of HPAL was purified in two iron removal stages under the determined optimum conditions. Nearly all of the Al and Cr were removed from the PLS in the two stages of iron removal. Then, nickel and cobalt were taken out from the PLS in the form of mixed hydroxide precipitates (MHP) in two stages. A MHP 1 product containing 33.41 wt.% Ni, 2.93 wt.% Co was obtained with a Mn contamination of 3.69 wt.% at the optimized conditions of pH=7, 50oC and 60 minutes. The MHP 1 product was also contaminated with Fe (2.83 wt.%) since it could not be completely removed from the PLS without the critical losses of nickel and cobalt during the two iron removal stages.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12613437/index.pdf |
| Date | 01 August 2011 |
| Creators | Secen, Berk |
| Contributors | Topkaya, Yavuz Ali |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.0022 seconds