This thesis presents a comparative study between two silver nanoparticle inks that were deposited using a Drop-on-Demand (DoD) inkjet printer, aiming at finding a functional ink that can be used to print electrodes in Light-emitting Electrochemical Cells (LECs). To achieve this, a DoD inkjet printer was installed and an acquaintance with the printer was attained. Among the two inks, one was employed as received while the other was reformulated, and successful deposition of both the inks was observed. During the reformulation process, it was seen that the highly volatile tetrahydrofuran (THF) solvent can be used to improve the ink properties, in contrast to what is recommended. After that, the inks were deposited on UV-ozone treated glass substrates, sintered at an elevated temperature under ambient conditions, and their specific resistances and thicknesses were measured. Finally, the inks were used to print the anode in a structured sandwich-cell LEC. The performance comparison was conducted by observing the emitted light of the LECs. The results indicate that the reformulated ink performs better, probably due to the lower silver concentration that results in flatter surface, which in turn effectively alleviates shorts.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:umu-62827 |
Date | January 2012 |
Creators | Nahid, Masrur Morshed |
Publisher | Umeå universitet, Institutionen för fysik |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds