Previous issue date: 2014-11-17 / O objetivo desse estudo foi analisar 1) o efeito do co-iniciador alternativo 4,4’bisdimetilaminobenzidrol
(BZN) no grau de conversão (GC) e nas propriedades
mecânicas e biológicas de resinas compostas experimentais e 2) a correlação entre
metodologias empregadas para o teste de GC de resinas compostas. Para o
Experimento 1, o co-iniciador BZN foi utilizado em três concentrações (0,2, 0,5 e
1,2), e o co-iniciador DMAEMA como controle, nas mesmas concentrações acima. A
concentração molar entre canforoquinona (CQ) e os co-iniciadores foi mantida
constante (1:1). As resinas compostas foram manipuladas e submetidas aos testes
de microdureza (VHN), resistência à compressão e flexural (em MPa), módulo de
elasticidade (em GPa), GC (em %, por meio de espectroscopia micro-Raman e FTIR
com KBr), citotoxicidade in vitro (frente às células fibroblásticas 3T3) e avaliação
in vitro da aderência de Candida albicans e Streptococcus mutans sobre as resinas
experimentais. Para o Experimento 2, foram utilizadas as três resinas experimentais
com DMAEMA (DMAEMA0,2, DMAEMA0,5 e DMAEMA1,2) foram submetidas a três
testes para avaliação de GC: espectroscopia micro-Raman, Infravermelho por
transformada de Fourier com aparelho de refletância total atenuada (FT-IR ATR) e
FT-IR com confecção de pastilhas de KBr (FT-IR KBr). Os resultados do
Experimento 1 foram submetidos ao teste ANOVA 1 fator e pós-teste de Tukey
(α=0,05) e os dados do Experimento 2 foram analisados por ANOVA 2 fatores
(concentração do co-iniciador x metodologia) e pós-teste de Tukey (α=0,05), e a
correlação entre as três metodologias foi analisada por regressão linear múltipla. A
significância da regressão e das variáveis independentes foi estimada por teste F e t,
respectivamente, com 95% de confiança. Os resultados do Experimento 1
mostraram que as resinas compostas experimentais com o BZN apresentaram GC e
propriedades mecânicas satisfatórias, além de serem consideradas atóxicas a
fibroblastos 3T3. Ainda, a avaliação de aderência de Candida albicans e
Streptococcus mutans revelou que as resinas com BZN apresentaram alto grau de
inibição em diluição, comparado ao controle DMAEMA; para o Experimento 2, o GC
das resinas compostas com o co-iniciador DMAEMA em diferentes concentrações
não apresentou diferenças; porém, as três metodologias estudadas apresentaram
forte correlação positiva (r2:0,95). Conclui-se que a inclusão do co-iniciador BZN
fornece potencial antimicrobiano à resina composta, sem comprometer o grau de
conversão e as propriedades mecânicas da mesma. E que as três metodologias
estudadas influenciaram os valores obtidos de GC, na sequência: micro-Raman >
FT-IR ATR > FT-IR com KBr. / The aim of this study was to examine 1) the effect of the alternative coinitiator 4,4'bis
dymethilaminobenzydrol (BZN) in degree of conversion (DC) and mechanical and
biological properties of experimental resin composites and 2) the correlation between
methods used to analyze DC of resin composites. In Experiment 1, the coinitiator
BZN was used in three concentrations (0.2, 0.5 and 1.2), and the coinitiator
DMAEMA as control at the same concentrations as above. The molar concentration
of camphorquinone (CQ) and coinitiators was kept constant (1:1). The composites
were manipulated and submitted to microhardness test (VHN), flexural and
compressive strength (in MPa), elastic modulus (GPa), DC (in %, by micro-Raman
spectroscopy and FT-IR), in vitro cytotoxicity (against 3T3 fibroblastic cells) and in
vitro evaluation of Candida albicans and Streptococcus mutans adhesion on the
experimental resins. In Experiment 2, the three experimental resins with DMAEMA
(DMAEMA0.2, DMAEMA0.5 and DMAEMA1.2) were used. The groups were
subjected to three tests to assess DC: micro-Raman spectroscopy, Fourier transform
infrared spectroscopy with attenuated total reflectance (FT-IR ATR) and FT-IR with
preparation of KBr pellets (FT-IR KBr). The results of Experiment 1 were subjected to
one-way ANOVA and Tukey post-test (α = 0.05) and data from Experiment 2 were
analyzed by two-way ANOVA (coinitiator concentration versus methodology) and
Tukey post-test (α = 0.05). The correlation between the three methods was analyzed
by multiple linear regression. The significance of the regression and the independent
variables was estimated by F and t tests, with 95% of confidence. The results of
Experiment 1 showed that the experimental composite resin with BZN showed
satisfactory DC and mechanical properties, and was considered nontoxic against 3T3
fibroblasts. Also, the evaluation of Candida albicans and Streptococcus mutans
adhesion revealed that BZN resins exhibited a high degree of inhibition compared to
control resins with DMAEMA; for Experiment 2, DC of composites with DMAEMA at
the three different concentrations did not show significant differences; however, the
three methodologies analyzed showed a strong positive correlation (r2: 0.95), It was
concluded that the inclusion of the coinitiator BZN provides antimicrobial potential to
resin composites, without compromising degree of conversion and mechanical
properties. Also, the three methodologies influenced DC values, as follows: micro-
Raman > FT-IR ATR > FT-IR with KBr.
| Identifer | oai:union.ndltd.org:IBICT/oai:tede2.uepg.br:prefix/2626 |
| Date | 17 November 2014 |
| Creators | Cunha, Bruna Fortes Bittencourt |
| Contributors | Gomes, Osnara Maria Mongruel, Farago, Paulo Vitor, Pinheiro, Luis Antonio, Pereira, Stella Kossatz, Santos, Elizabete Brasil dos, Netto, Camillo Anauate, Vasconcelos, Andrea Freire de |
| Publisher | Universidade Estadual de Ponta Grossa, Programa de Pós-Graduação em Odontologia, UEPG, Brasil, Departamento de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UEPG, instname:Universidade Estadual de Ponta Grossa, instacron:UEPG |
| Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds