Orientador: Jose Roberto Lovadino / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-15T04:10:10Z (GMT). No. of bitstreams: 1
Fragoso_LarissaSilveiradeMendonca_D.pdf: 5875751 bytes, checksum: fa7d309c1cc22de111d7f7c71f8d04c5 (MD5)
Previous issue date: 2010 / Resumo: Os objetivos deste estudo "in vitro" foram: 1) avaliar o efeito da microabrasão sobre a microdureza e a rugosidade do esmalte dental bovino, bem como a ação do polimento realizado com pastas apropriadas no esmalte abrasionado; 2) avaliar o armazenamento em saliva artificial, em diferentes tempos de ação sobre a microdureza do esmalte dental bovino. Para isso, foram utilizados 144 blocos de esmalte bovino (6,0mm x 6,0mm) que constituíram os grupos: I- tratamento com ácido fosfórico a 37% e pedra pomes (n=48), II- tratamento com Opalustre (Ultradent) (n=48), III- tratamento com Whiteness RM (FGM) (n=48). Os três grupos foram divididos em três subgrupos, de acordo com os seguintes tratamentos: a) polimento com pasta diamantada; b) polimento com pasta profilática fluoretada e c) sem polimento (controle). Foram realizados ensaios de microdureza nos seguintes tempos estabelecidos: 1) inicial (antes da realização da microabrasão e polimento); 2) após a realização da microabrasão com e sem polimento; 3) após a realização da microabrasão com e sem polimento e imersão em saliva artificial por períodos de 24 horas; 4) após a realização da microabrasão com e sem polimento e imersão em saliva artificial por 7 dias. Foram realizados ensaios de rugosidade nos seguintes tempos pré-estabelecidos: 1) inicial (antes da realização da microabrasão e polimento) e final (após a realização da microabrasão com e sem polimento (controle). Os dados obtidos foram submetidos à análise estatística ANOVA "dois fatores", e teste de Tukey com significância de 5% para microdureza e rugosidade. Os resultados mostraram que a microabrasão seguida de polimento proporcionou aumento de microdureza superficial; quando não se utilizou polimento, somente os sistemas microabrasivos com ácido clorídrico e carbeto de silício apresentaram aumento da microdureza superficial; os diferentes tempos de armazenamento em saliva artificial não resultaram em aumento da microdureza superficial; os produtos utilizados para microabrasão não proporcionaram rugosidade superficial diferentes entre si; todos os sistemas microabrasivos seguidos de polimento apresentaram maior lisura superficial quando comparados aos grupos sem polimento. Baseado nos resultados obtidos, conclui-se que a microabrasão seguida de polimento, proporcionou maior dureza e maior lisura de superfície do esmalte dental. A imersão em saliva artificial por períodos de 24 horas e 7 dias, contudo, não alterou a dureza do esmalte dental. / Abstract: The objectives of this study in vitro were: 1) evaluate the effect of microabrasion on microhardness and roughness of bovine enamel and the action of polishing carried out with the appropriate pastes on abrasioned enamel, 2) evaluate the effect of storage in artificial saliva, during different times of action, on the microhardness of bovine dental enamel. For this, used 144 bovine enamel blocks (6.0 mm x 6.0 mm), forming the groups: I-treatment with 37% phosphoric acid and pumice paste (n = 48), Il-treatment with Opalustre (Ultradent) (n = 48), Ill-treatment with Whiteness RM (FGM) (n = 48). Then the three groups were divided into three subgroups, according to the following treatments: a) diamond polishing paste, b) polishing with fluoride prophylactic paste and c) without polishing (control). Tests of hardness were carried out in the following set times: 1) initial (prior to the microabrasion and polishing), 2) after microabrasion with and without polishing (control), 3) after microabrasion with and without polishing and immersion in artificial saliva for 24 hours; 4) after microabrasion with and without polishing and immersion in artificial saliva for 7 days. Tests of surface roughness were performed in the following pre-set times: 1) initial (prior to the microabrasion and polishing) and final (after the completion of microabrasion with and without polishing) (control). The obtained data were analyzed by "two factors" ANOVA and Tukey test with significance of 5% for hardness and roughness. The results showed that: microabrasion followed by polishing provided an increase of superficial microhardness; without the use of polishing, only the microabrasive systems with hydrochloric acid and silicon carbide showed increased superficial microhardness; different times of storage in artificial saliva did not result in increased microhardness; the products used for microabrasion did not provide surface roughness different from each other; all microabrasive systems followed by polishing showed a higher surface smoothness compared with the groups without polishing. Based on these results, it can be inferred that microabrasion followed by polishing provided higher hardness and better surface smoothness of the dental enamel. However, the immersion in artificial saliva for 24 hours and 7 days was not able to increase the enamel hardness. / Doutorado / Dentística / Doutor em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289452 |
| Date | 02 September 2010 |
| Creators | Fragoso, Larissa Silveira de Mendonça |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Lovadino, José Roberto, 1953-, França, Fabiana Mantovani Gomes, Sundfeld, Renato Hermann, Aguiar, Flávio Henrique Baggio, Lima, Débora Alves Nunes Leite |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 74 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds