Orientadores: Rafael Leonardo Xediek Consani, Mateus Bertolini Fernandes dos Santos / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-24T21:15:14Z (GMT). No. of bitstreams: 1
Nogueira_MoisesdaCostaFerraz_M.pdf: 1749031 bytes, checksum: 8fa4481a045e127aabb629294129a5b0 (MD5)
Previous issue date: 2014 / Resumo: O objetivo neste estudo foi avaliar por meio da análise por elemento finito 3-D, as tensões ocorridas em overdentures com sistemas de retenção barra-clipe, quando diferentes formas da seção transversal (circular, ovóide ou Hader) apresentam diferentes níveis de desajuste vertical (50, 100 e 200 µm) e são confeccionadas com diferentes ligas metálicas (Au tipo IV, Ag-Pd, Co-Cr e Ti cp). Modelos tridimensionais foram feitos utilizando software para modelagem 3-D (SolidWorks 2010) e importados para o software de simulação mecânica (ANSYS Workbench 11). Aperto simulado do parafuso foi realizado até obter assentamento adequado entre infraestrutura e plataforma protética. As análises foram realizadas com o objetivo de obter as tensões Máxima Principal e de von Mises (MPa). Os valores da tensão aumentaram com o aumento do desajuste vertical, assim como a barra Hader proporcionou os maiores valores. Barras circulares feitas com Au tipo IV causaram os menores valores na barra e no parafuso protético. Ligas resilientes mostraram melhores resultados que as rígidas, enquanto a maior complexidade da seção transversal da barra e o maior nível de desajuste vertical aumentaram a concentração das tensões na barra, parafuso protético e tecido ósseo cortical. Conclui-se que as tensões induzidas na barra, parafuso protético e tecido ósseo peri-implantar foram influenciadas pelo aumento do desajuste vertical, complexidade da seção transversal e liga da barra / Abstract: The objective of this study was to evaluate by 3-D finite element analysis tensions occurred in overdentures with bar-clip retention systems, when different cross-sectional geometries (circular, oval or Hader) have different levels of vertical misfit (50, 100 and 200 µm) and were maded from different metallic alloys (type IV Au , Ag-Pd , Co-Cr and Ti cp). Three-dimensional models were maded using 3-D modeling software (SolidWorks 2010) and imported into the software of mechanical simulation (ANSYS Workbench 11). A displacement simulating screw tightening was done until proper fitting of the prosthetic platform infrastructure. The analyzes were performed in order to obtain the Maximum Principal Stress and von Mises (MPa). The stress values increased proportionally with the level of vertical misfit and Hader bar showed the highest values. Circular bars made with Au type IV showed the lowest values on the bar and prosthetic screw. Resilient alloys performed better than hard, while the greater complexity of the cross section of the bar and the highest levels of vertical misfit increased stress concentration on the infrastructure of the bar, prosthetic screw and cortical bone tissue. The stress induced on the bar, prosthetic screw and peri-implant bone tissue were influenced by increased vertical misfit, complexity of cross section and different alloys of the bar / Mestrado / Protese Dental / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288565 |
| Date | 06 June 2014 |
| Creators | Nogueira, Moises da Costa Ferraz, 1989- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Santos, Mateus Bertolini Fernandes dos, 1985-, Consani, Rafael Leonardo Xediek, 1974-, Mesquita, Marcelo Ferraz, Reis, José Maurício dos Santos Nunes |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 55 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds