Previous issue date: 2012-02-28 / Este estudo teve como objetivo avaliar quatro técnicas de inserção de cimento
resinoso na retenção de pinos de fibra de vidro à dentina radicular nos diferentes
terços radiculares, bem como a nanoinfiltração nestes diferentes terços. As raízes de
cinqüenta e dois pré-molares inferiores humanos extraídos foram tratadas
endodonticamente e padronizado o preparo dos condutos. Assim, elas foram
divididas aleatoriamente em quatro grupos, de acordo com a técnica de inserção do
cimento: GC - seringa Centrix® com ponta fina; GL - broca Lentulo 35, GP - cimento
aplicado diretamente no pino e GI - seringa para aplicação de insulina. Os pinos
intra-radiculares (White Post DC - FGM) tiveram suas superfícies tratadas de acordo
com o fabricante e foram cimentados de acordo com cada técnica. Após o
armazenamento em água a 37° C por uma semana, para cada grupo, dez raízes
foram seccionadas transversalmente em seis discos com 1 mm de espessura cada,
e os terços coronário (TC), médio (TM) e apical (TA) do canal radicular foram
identificados. O teste de push-out foi realizado a uma velocidade de 0,5 mm/min.
Para avaliação da nanoinfiltração três raízes de cada grupo, ou seja, 6 discos por
raiz, foram submetidos a imersão em Nitrato de Prata 50% para posterior obtenção
de imagens feitas em microscopia eletrônica de varredura. As imagens foram
analisadas por meio de software apropriado para obtenção das médias dos valores
de nanoinfiltração convertidas em porcentagem. Os dados, submetidos a análise
estatística por ANOVA 1 fator e Pós-teste Tukey (0,5%), mostraram que GC
apresentou os melhores valores para resistência adesiva (MPa) e nanoinfiltração
(%): 18,57 ± 4,19 e 37,70 ± 18,95 respectivamente, tendo GP o pior desempenho:
13,71 ± 1,61 e 65,11 ± 13,58 respectivamente. A técnica de inserção do cimento
resinoso teve influencia nos valores de resistência adesiva e nanoinfiltração
encontrados no estudo. / The aim of this study was to evaluate four techniques for insertion of resin cement on
retention of glass fiber posts to root dentin in different root thirds, as well as these
different nanoleakage in adhesive interface. The roots of the fifty-two human
extracted pre-molars were endodontically treated and standardized preparation of the
canals. It were divided into four groups according to the technique of insertion of the
cement: GC - Centrix ® syringe with fine tip, GL - # 35 drill Lentulo, GP - cement
applied directly to the post and GI - syringe for insulin delivery. The posts (White Post
DC - FGM) had their surfaces treated in accordance with the manufacturer and were
cemented according to each technique. After storage in water at 37° C for one week,
each group of ten roots were sectioned transversely into six discs with 1 mm thick
each, and coronal thirds (CT), medium (TM) and apical (TA) of root canal were
identified. The push-out test was conducted at a speed of 0.5 mm / min. To evaluate
the nanoleakage in the adhesive interface, three roots of each group, ie, 6 slices per
root were submitted to immersion in 50% silver nitrate for subsequent obtaining of
images made using scanning electron microscopy. Images were analyzed using
appropriate software to obtain the mean nanoleakage values converted into
percentage. The data were subjected to statistical analysis by ANOVA (one factor)
and Tukey post-test (0.5%), showed that GC had the best values for bond strength
(MPa) and nanoleakage (%):18,57 ± 4,19 e 37,70 ± 18,95 repectively and GP had
the worst values: 13,71 ± 1,61 e 65,11 ± 13,58 respectively. The insertion technique
of resin cement influenced on the bond strength values and on the nanoleakage
found in the study.
| Identifer | oai:union.ndltd.org:IBICT/oai:tede2.uepg.br:prefix/2639 |
| Date | 28 February 2012 |
| Creators | Dobrovolski, Max |
| Contributors | Gomes, Osnara Maria Mongruel, Gomes, João Carlos, Albuquerque, Rodrigo de Castro |
| Publisher | Universidade Estadual de Ponta Grossa, Programa de Pós-Graduação em Odontologia, UEPG, Brasil, Departamento de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UEPG, instname:Universidade Estadual de Ponta Grossa, instacron:UEPG |