Orientador: Pascoal Jose Giglio Pagliuso / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin / Made available in DSpace on 2018-08-15T21:09:50Z (GMT). No. of bitstreams: 1
Bittar_EduardoMatzenbacher_D.pdf: 12237565 bytes, checksum: 74dcda9fcb1da9b6fc8d992b53297127 (MD5)
Previous issue date: 2010 / Resumo: Séries de compostos que apresentam a ocorrência de fenômenos físicos interessantes em materiais estruturalmente simples constituem uma excelente oportunidade para se estudar sistematicamente a inter-relação entre tais fenômenos e suas origens microscópicas, sem se ater a efeitos associados com estruturas cristalinas complexas, de mais baixa simetria. Nesse sentido, esta Tese se propôs a estudar três temas de investigação: o sistema CeIn3-xSnx e o seu análogo não magnético LaIn3-xSnx, o sistema CeIn3-xCdx e o composto YbAl3 e o seu composto de referência LuAl3.
O sistema CeIn3-xSnx apresenta um ponto crítico quântico (QCP) em x ? 0.7, onde a ordem antiferromagnética (TN = 10 K no CeIn3) é totalmente suprimida. Para 0.7 < x < 2 os compostos são líquidos de Fermi e a partir de x = 2 apresentam valência intermediária. Nesse sistema, dopado com Gd3+, medidas de ressonância de spin eletrônico (ESR) indicaram que o elétron 4f do Ce passa de um comportamento com momento localizado para itinerante com a dopagem de Sn. Os resultados de ESR do Gd3+ no sistema LaIn3-xSnx foram analisados com um modelo de uma única banda (tipo s) e sem dependência com a transferência de momento.
Também investigamos o sistema CeIn3-xCdx através de medidas de susceptibilidade magnética, calor específico e resistividade elétrica. A substituição do In por Cd diminui a TN do CeIn3 e igualmente faz o coeficiente do calor específico eletrônico decrescer, indicando que o sistema não está na direção de um QCP.
Os compostos YbAl3 e LuAl3, dopados com Gd3+, também foram estudados por ESR, porém, na análise, utilizou-se um modelo de múltiplas bandas para explicar os resultados. Medidas de calor específico e susceptibilidade magnética, nessas amostras, mostraram que interações de troca elétron-elétron estão presentes em ambos os compostos. Esses resultados microscópicos podem ser importantes em modelos teóricos mais realistas para materiais férmions pesados de valência intermedi'aria a base de Yb / Abstract: Series of compounds which have interesting physical phenomena, occurring in structurally simple materials, provide an excellent opportunity to systematically study the interrelationship between these phenomena and their microscopic origins, without worrying about effects associated with other complex crystal structures of lower symmetry. Thus, this thesis set out to study three research themes: the CeIn3-xSnx system and its nonmagnetic analogue LaIn3-xSnx, the CeIn3-xCdx system and the YbAl3 compound and its reference compound LuAl3.
The CeIn3-xSnx system has a quantum critical point (QCP) at x ? 0.7, where the antiferromagnetic order (TN = 10 K in CeIn3) is totally suppressed. For 0.7 < x < 2 the compounds are Fermi liquids and from x = 2 the materials show intermediate valence behavior. In this system, doped with Gd3+, measurements of electron spin resonance (ESR) indicated that the Ce 4f electron presents a crossover between a localized to itinerant behavior with Sn doping. The ESR results of Gd3+ in the LaIn3-xSnx system were analyzed with a single band model (s type) and no q dependence.
We also investigated the CeIn3-xCdx system by measuring magnetic susceptibility, specific heat and electrical resistivity proprieties. The substitution of In by Cd decreases the TN of CeIn3 and also decreases the electronic specific heat coefficient, indicating that the system is not being tuned to a QCP.
The YbAl3 and LuAl3 compounds, doped with Gd3+, were also studied by ESR, but in the analysis, we used multiband model to explain the results. Specific heat and magnetic susceptibility measurements in these samples showed that electron-electron exchange interactions are present in both compounds. These ESR results may be relevant to construct more realistic models of the microscopic behavior of other heavy fermion-based intermediate valence Yb compounds / Doutorado / Física da Matéria Condensada / Doutor em Ciências
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/278539 |
Date | 15 August 2018 |
Creators | Bittar, Eduardo Matzenbacher |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Pagliuso, Pascoal José Giglio, 1971-, Salazar, Nelson Orlando Moreno, Ávila, Marcos de Abreu, Lima, Oscar Ferreira de, Rodrigues, Varlei |
Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 115 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds