Mitigação da reação álcali-agregado em concreto com o emprego de resíduo de cerâmica vermelha e metacaulim

Submitted by JOSIANE SANTOS DE OLIVEIRA (josianeso) on 2017-06-20T12:30:42Z
No. of bitstreams: 1
Moisés Mário Cachepa_.pdf: 3004067 bytes, checksum: 24c7ce290fa414a34e3454c918c0403c (MD5) / Made available in DSpace on 2017-06-20T12:30:42Z (GMT). No. of bitstreams: 1
Moisés Mário Cachepa_.pdf: 3004067 bytes, checksum: 24c7ce290fa414a34e3454c918c0403c (MD5)
Previous issue date: 2017-05-22 / CNPQ – Conselho Nacional de Desenvolvimento Científico e Tecnológico / O uso de adições minerais, como as pozolanas, tem sido adotado como adição ou substituição parcial do cimento, fundamentalmente na produção de concretos, com intuito de melhorar algumas das características, tais como redução de calor de hidratação, melhoria da trabalhabilidade, aumento da resistência à compressão, aumento da durabilidade em meios agressivos, redução da emissão de CO2, redução do aparecimento de eflorescência. Um sério problema de durabilidade é a reação álcali-agregado (RAA), que é um fenômeno que em geral se manifestam em estruturas de concreto massa, como barragens. A RAA é entendida como sendo um processo químico que ocorre em concreto, em que alguns constituintes mineralógicos presentes no agregado reagem com íons alcalinos, provenientes de hidróxidos originados na hidratação do cimento que estão dissolvidos na solução dos poros, formando um gel higroscópico expansivo. Este trabalho teve como objetivo avaliar a mitigação da reação álcali-agregado em concreto mediante o emprego de resíduos da cerâmica vermelha (RCV) e metacaulim (MK) como pozolanas. O RCV foi adquirido como resíduo de indústria da produção de blocos cerâmicos, enquanto que o MK é um produto comercializado, sabidamente mitigador da RAA e, geralmente, com elevada atividade pozolânica. Para se alcançar o objetivo, foram analisadas as características físicas, químicas, mineralógicas do RCV e do MK, e determinou-se o índice da atividade pozolânica. Tanto o RCV como o MK apresentaram índice de atividade pozolânica superior a 90%. O agregado utilizado foi classificado como potencialmente reativo por meio de análise de petrografia e do método acelerado de barras de argamassa. Para avaliação da eficiência das adições minerais na mitigação da RAA, empregou-se o método acelerado de barras de argamassa. As pozolanas isoladas e combinadas foram empregadas em teores de substituição de cimento de 20% e 30%. Avaliou-se também resistência à compressão e absorção capilar de água em 48h e 28 dias, submetidos à solução saturada de em Ca(OH)2; e em 28 dias de imersão em solução de NaOH. Com os resultados de expansão, foi possível verificar que todos os materiais e teores propostos promoveram uma mitigação da RAA em relação às amostras confeccionadas somente com cimento, com valores de expansão inferiores a 0,10%. Para os aglomerantes estudados, foi possível verificar que entre as pozolanas, quanto menor o equivalente alcalino, menores são as expansões. No entanto, as misturas somente com MK apresentam valores de equivalente alcalino similares ao cimento e as expansões são significativamente reduzidas. Para uma mesma relação Ca/Si dos aglomerantes, quanto maior for o teor de RCV menor é a expansão. Quando se avalia o teor de alumina dos aglomerantes, percebe-se que aqueles que contém MK apresentam o maior teor, mas, no entanto, não retornam as menores expansões, o que se explica pela sua maior dimensão média equivalente, em relação aos aglomerantes que contém RCV. A menor dimensão das partículas de RCV parecem aumentar o efeito mitigador que o teor de Al possui, pois a superfície de dissolução destas partículas é maior. A comparação dos resultados da resistência à compressão e absorção de água antes de iniciar o ensaio acelerado e após, bem como a comparação com as argamassas aos 28 dias que não sofreram ataques ajudam a enteder o comportamento das pozolanas na mitigação da RAA. / The use of mineral additions through pozzolans, both naturally and artificially, has been adopted by several civil engineering professionals through the partial substitution of cement primarily in the production of concrete slabs, with the aim of improving some of the characteristics such as: Reduction of the heat of hydration, improvement of the workability, increase of the resistance to compressive strength, increase of the durability in aggressive environments, reduction of the emission of CO2, reduction of the appearance of efflorescence and reduction of the expansions due to the alkali-aggregate reactions. One of the pathologies that greatly affects mass concrete structures such as dams is the alkali-aggregate reaction, which is understood to be a chemical process occurring in concrete, in which some mineralogical constituents present in the aggregate react with hydroxides from the cement that are dissolved In the solution of the pores forming an expansive hygroscopic gel. The elaboration of this work, on the one hand, was motivated by the fact that one of the main dams in Africa located in Mozambique, shows signs of expansion according to several authors and, on the other hand, as a way of evaluating the Pozolan potential of RCV and MK. This work aimed to evaluate the mitigation of the alkali-aggregate reaction in concrete through the use of residues of red ceramics and metakaolin as pozzolans. The RCV was purchased as a waste from the production of ceramic blocks, while the MK was from a commercial product. In order to reach the objective, the RCV and MK underwent an investigation taking into account physical, chemical, mineralogical characteristics and the determination of the index of the pozzolanic activity. Both RCV and MK had pozzolanic activity index higher than the 90% established by NBR 12653 (2014). The aggregate used was classified as potentially reactive through analyzes of petrography, DRX, FRX and accelerated method of mortar bars. For the evaluation of RAA, samples were prepared and analyzes of aggregate reactivity and mineral additions efficiency were performed using the accelerated method of mortar bars, compressive strength and water capillary absorption in a substitution of 20% and 30% of cement by RCV, MK and RCV + MK, in the following curing ages: 48h, 28 days in Ca (OH) 2 and 28 days of immersion in NaOH solution. By the expansion results, it was possible to verify that all materials and cement substitution contents by pozzolans proposed had a reduction of less than 0.10% recommended by ASTM C1567 (2013), classified as insufficient to cause deleterious reactions due to potential Pozolânico of the MK and RCV. It was possible to verify that the higher the alkaline equivalent, the larger the expansions, the smaller the Ca / Si ratio, the smaller the expansions, the higher the alumina content, the smaller the expansions, the smaller the average equivalent size Of the particles, the smaller the expansions, and the larger the total porosity, the larger the expansions. The results of the compressive strength and water absorption showed that the mixtures submitted to the accelerated test presented worse performance in relation to the cured mixtures in Ca (OH) 2 due to the microstructure of the mortars, creating internal microcracks, or because the formed gel permeable to water penetration.

Identiferoai:union.ndltd.org:IBICT/oai:www.repositorio.jesuita.org.br:UNISINOS/6360
Date22 May 2017
CreatorsCachepa, Moisés Mário
Contributorshttp://lattes.cnpq.br/7718312732162781, Abreu, Aguida Gomes de
PublisherUniversidade do Vale do Rio dos Sinos, Programa de Pós-Graduação em Engenharia Civil, Unisinos, Brasil, Escola Politécnica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UNISINOS, instname:Universidade do Vale do Rio dos Sinos, instacron:UNISINOS
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0034 seconds