Orientador: Vladimir Antonio Paulon / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil / Made available in DSpace on 2018-07-22T09:49:17Z (GMT). No. of bitstreams: 1
Zordan_SergioEduardo_M.pdf: 4136779 bytes, checksum: 835f8d2cedda9b692211727d7fedbfb5 (MD5)
Previous issue date: 1997 / Resumo: Os resíduos produzidos pela indústria da construção civil passam, cada vez mais, a serem vistos como uma fonte alternativa de matéria prima, a ser reutilizada no setor. Dessa forma, incentivando esse processo e oferecendo bases científicas para o seu fortalecimento, realizou-se um estudo com o objetivo de analisar a reciclagem da parte mineral do entulho, utilizando-a como agregado na confecção do concreto. O resíduo utilizado, proveniente de uma usina de reciclagem de entulho, foi analisado granulométrica e qualitativamente, de modo a ser classificado como um agregado. Com esse material, produziu-se concreto em diferentes traços e relações água/ cimento, que foram ensaiados à compressão simples, à abrasão e à permeabilidade, em idades distintas. Os testes mostraram que, à medida que se diminuiu o consumo do cimento, a resistência à compressão se aproximou dos valores obtidos pelo concreto de referência, enquanto que a resistência à abrasão mostrou-se melhor em todos os casos onde se usou entulho como agregado. Os resultados do trabalho permitiram concluir que o entulho pode ser utilizado como agregado, na confecção de concreto não estrutural destinados à infra-estrutura urbana. ...Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: The waste generated by the civil engineering industry has been seen on an increasing form as an alternative source of raw material to be used in this sector. Therefore, giving an incentive to this. process and offering scientific data to its strengthening, it was studied the recycling of the mineral part of construction and demolition (C&D) wastes, and its use as concrete aggregate. The waste was got in a MFR (materiais recovery facilities) and than it was analized according to the size and the nature of its particles. With this material it was produced concrete with differents amounts of cement, aggregate and water/ cement ratio, which were tested to compression, abrasion and permeability, at different ages. The tests have shown that, with the decrease of the cemente rate, the compressive strength was near to the reference concrete. The abrasion resistance was higher than conventional concrete in ali analized cases. The experimental results indicated that the wastes of C&D can be used like aggregate to the production of no reinforced concrete to urban infra structure. ...Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Saneamento / Mestre em Engenharia Civil
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/258458 |
| Date | 18 February 1997 |
| Creators | Zordan, Sergio Eduardo |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Paulon, Vladimir Antonio, 1938-, Teixeira, Eglé Novaes, Beraldo, Antônio Ludovico |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Civil, Programa de Pós-Graduação em Engenharia Civil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 140f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.4033 seconds