Previous issue date: 2012-04-11 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / Oxygen carriers are metal oxides which have the ability to oxidize and reduce
easily by various cycles. Due to this property these materials are widely usedin
Chemical-Looping Reforming processes to produce H2 and syngas. In this work
supports based on MCM-41 and La-SiO2 were synthesized by hydrothermal method.
After the synthesis step they were calcined at 550?C for 2 hours and characterized by
TG, XRD, surface area using the BET method and FTIR spectroscopy. The
deposition of active phase, in this case Nickel, took place in the proportions of 5, 10
and 20% by weight of metallic nickel, for use as oxygen carriers.The XRD showed
that increasing in the content of Ni supported on MCM-41 resulted in a decrease in
spatial structure and lattice parameter of the material. The adsorption and desorption
curves of the MCM-41 samples exhibited variations with the increase of Ni deposited.
Surface area, average pore diameter and wall density of silica showed significant
changes , due to the increase of the active phase on the mesoporous material. By
other hand, in the samples with La-SiO2 composition was not observed peaks
characteristic of hexagonal structure, in the XRD diffractogram. The
adsorption/desorption isotherms of nitrogen observed are type IV, characteristic of
mesoporous materials. The catalytic test indicates that the supports have no
influence in the process, but the nickel concentration is very important, because the
results for minor concentration of nickel are not good. The ratio H2/O2 was close to 2,
for all 15 cycles involving the test storage capacity of O2, indicating that the materials
are effective for oxygen transport / Transportadores de oxig?nio s?o ?xidos met?licos que possuem a capacidade
de oxidar e reduzir facilmente por diversos ciclos. Devido a essa propriedade estes
materiais s?o bastante utilizados nos processos de Chemical-Looping Reforming
para a produ??o de H2 ou g?s de s?ntese (H2 mais CO). Neste trabalho foram
sintetizados os suportes MCM-41 e La-SiO2 pelo o m?todo hidrot?rmico. Os
materiais resultantes foram calcinados a 550 ?C por 2 horas e, posteriormente,
caracterizados por TG, DRX, ?rea superficial pelo m?todo BET e FTIR. Ap?s a
caracteriza??o dos suportes foi feita a deposi??o da fase ativa (Ni) com as
propor??es de 5, 10 e 20% em massa de n?quel met?lico, para aplica??o como
transportadores de oxig?nio. As an?lises de DRX mostraram que o aumento do teor
de Ni suportado em MCM-41 deu origem a uma diminui??o no ordenamento
estrutural e no par?metro de rede do material. As amostras MCM-41 apresentaram
varia??es quanto ?s curvas de adsor??o/dessor??o de nitrog?nio, ?rea superficial,
di?metro m?dio de poros e espessura da parede de s?lica, em fun??o do aumento da
fase ativa no material mesoporoso. Enquanto que nas amostras com La-SiO2 n?o se
observou picos caracter?sticos da estrutura hexagonal, nos difratogramas de DRX.
Entretanto, as curvas de adsor??o/dessor??o de nitrog?nio observadas s?o do tipo
IV, caracter?stico de materiais mesoporosos. Os resultados dos testes dos
transportadores indicam que o suporte n?o influenciou no processo catal?tico. A
raz?o H2/O2 foi pr?xima de 2, durante todos os 15 ciclos envolvendo o teste de
capacidade de armazenamento de O2 , indicando que os materiais s?o eficientes
para o transporte de oxig?nio
estrutural e no par?metro de rede do material. As amostras MCM-41 apresentaram
varia??es quanto ?s curvas de adsor??o/dessor??o de nitrog?nio, ?rea superficial,
di?metro m?dio de poros e espessura da parede de s?lica, em fun??o do aumento da
fase ativa no material mesoporoso. Enquanto que nas amostras com La-SiO2 n?o se
observou picos caracter?sticos da estrutura hexagonal, nos difratogramas de DRX.
Entretanto, as curvas de adsor??o/dessor??o de nitrog?nio observadas s?o do tipo
IV, caracter?stico de materiais mesoporosos. Os resultados dos testes dos
transportadores indicam que o suporte n?o influenciou no processo catal?tico. A
raz?o H2/O2 foi pr?xima de 2, durante todos os 15 ciclos envolvendo o teste de
capacidade de armazenamento de O2 , indicando que os materiais s?o eficientes
para o transporte de oxig?nio
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/17736 |
| Date | 11 April 2012 |
| Creators | Costa, Tiago Roberto da |
| Contributors | CPF:06117988320, http://lattes.cnpq.br/3318871716111536, Barros, Joana Maria de Farias, CPF:85239658404, http://lattes.cnpq.br/1016070459137884, Ruiz, Juan Alberto Chavez, CPF:00744293456, http://lattes.cnpq.br/5051286289341242, Freitas, J?lio Cezar de Oliveira, CPF:00957245408, http://lattes.cnpq.br/2357217530716519, Melo, Dulce Maria de Ara?jo |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Qu?mica, UFRN, BR, F?sico-Qu?mica; Qu?mica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0013 seconds