Orientador: Marcelo Ferraz Mesquita / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T19:45:53Z (GMT). No. of bitstreams: 1
Takahashi_JessicaMieFerreiraKoyama_M.pdf: 3156848 bytes, checksum: e45be536e6455880f4523ac84c0d2894 (MD5)
Previous issue date: 2009 / Resumo: O objetivo neste estudo foi avaliar o efeito de diferentes tempos de envelhecimento acelerado realizado por meio da simulação do intemperismo natural, sobre as propriedades de deformação permanente e resistência à tração da união de dois materiais resilientes usados como forradores de base de prótese, sendo um à base de resina acrílica e outro à base de silicone. Para o ensaio de resistência à tração da união, os materiais reembasadores foram unidos a dois blocos de resina acrílica (9 X 9 X 40 mm) utilizada para a confecção de bases de próteses totais. Para o ensaio de deformação permanente, os corpos-de-prova de reembasador resiliente apresentaram 19 mm de altura e 12,7 mm de diâmetro. Os corpos-de-prova (n=10) foram submetidos ao envelhecimento acelerado nos tempos 2, 4, 8, 16, 32 e 64 ciclos por meio da simulação do intemperismo natural. O ensaio de resistência à tração da união foi realizado em máquina de ensaios EMIC DL-500 MF com velocidade média de 5 mm/min, sendo avaliado também o tipo de falha de união (adesiva, coesiva ou mista). Para o ensaio de deformação permanente foi utilizado aparelho mecânico descrito na especificação no 18 da A.D.A., com carga compressiva de 750 gf. Foi realizada análise estatística utilizando o teste Kruskall-Wallis associado ao método de Dunn, para comparação entre os materiais no mesmo intervalo de envelhecimento, e o teste Mann-Whitney para comparação do efeito dos tempos de envelhecimento em cada material. Avaliando os resultados obtidos após a análise estatística, pôde-se observar que o reembasador à base de silicone apresentou menor porcentagem de deformação permanente (p<0,0001) e maior resistência à tração (p<0,0001) que o reembasador à base de resina acrílica em todos os intervalos de envelhecimento. E que a simulação do intemperismo natural não afetou a deformação permanente (p=0,90) e a resistência à tração (p=0,15) do reembasador à base de silicone, mas reduziu a porcentagem de deformação permanente e aumentou a resistência à tração do material à base de resina acrílica (p<0,05). Os resultados demonstraram que o reembasador resiliente à base de silicone é menos susceptível à cargas compressivas, pois apresentou melhor recuperação elástica, menor deformação permanente e maior resistência à tração que o à base de resina acrílica. E que o envelhecimento acelerado, afeta as propriedades de deformação permanente e resistência à tração do material reembasador à base de resina acrílica. / Abstract: This study aimed to evaluate the effect of different times of accelerated ageing over the properties of permanent deformation and tensile bond strength of two soft liners used on prostheses relining. The soft liners studied were auto-polymerizing and acrylic resin and silicone based. The materials were processed according the manufacturers' instructions. The resilient liner specimens (9 X 9 X 3 mm) for tensile bond strength were processed between 2 acrylic resin blocks (9 X 9 X 40 mm). The resilient liner specimens for permanent deformation test were 19 mm height and 12.7 mm diameter. The specimens (n=10) were submitted to accelerated ageing process during 2, 4, 8, 16, 32 and 64 cycles. Tensile bond strength was performed with crosshead speed of 5 mm/min using a testing machine EMIC DL-500 MF. Permanent deformation was performed with an apparatus described on specification no 18 of A.D.A., with compressive load of 750 gf. Statistical analysis was performed using Kruskall-Wallis and Dunn tests to compare materials on the same ageing period and Mann-Whitney test to compare the effect of different ageing periods on each material. The results obtained after statistical analysis demonstrated that the silicone based reliner presented lower percentage of permanent deformation (p<0.0001) and higher tensile bond strength (p<0.0001) than the acrylic resin based reliner in all the ageing intervals. And that the accelerated ageing process did not affect the permanent deformation (p=0.90) and tensile bond strength (p=0.15) of the silicone based reliner, but reduced the percentage of permanent deformation and increased tensile bond strength of the acrylic resin based reliner (p<0.05). Results demonstrated that silicone based reliner is less susceptible to compressive loads, presenting better elastic recovery, lower permanent deformation and higher tensile bond strength. And that accelerated ageing affected only acrylic resin based reliners. / Mestrado / Protese Dental / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289906 |
| Date | 02 May 2009 |
| Creators | Takahashi, Jessica Mie Ferreira Koyama |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Mesquita, Marcelo Ferraz, 1967-, Goiato, Marcelo Coelho, Consani, Rafael Leonardo Xediek |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 87 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0119 seconds