Five well-known Zr-based alloys of the systems Zr–Cu–Al–(Ni–Nb, Ni–Ti, Ag) (Cu 5 15.4–36 at.%) with the highest glass-forming ability were comparatively analyzed regarding their pitting corrosion resistance and repassivation ability in a chloride-containing solution. Potentiodynamic polarization measurements were conducted in the neutral 0.01 M Na₂SO₄ 1 0.1 M NaCl electrolyte and local corrosion damages were subsequently investigated with high resolution scanning electron microscopy (HR-SEM) coupled with energy dispersive x-ray spectroscopy (EDX). Both pitting and repassivation potential correlate with the Cu concentration, i.e., those potentials decrease with increasing Cu content. Pit morphology is not composition dependent: while initially hemispherical pits then develop an irregular shape and a porous rim. Corrosion products are rich in Cu, O, and often Cl species. A combination of low Cu and high Nb or Ti contents is most beneficial for a high pitting resistance of Zr-based bulk metallic glasses. The bulk glassy Zr₅₇Cu₁₅.₄Al₁₀Ni₁₂.₆Nb₅ (Vit 106) and Zr₅₂.₅Cu₁₇.₉Al₁₀Ni₁₄.₆Ti₅ (Vit 105) alloys exhibit the highest pitting resistance.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:70547 |
| Date | 17 April 2020 |
| Creators | Gostin, Petre Flaviu, Eigel, Dimitri, Grell, Daniel, Eckert, Jürgen, Kerscher, Eberhard, Gebert, Annett, Scudino, S., Yang, C., Eckert, J. |
| Publisher | Cambridge University Press |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, doc-type:article, info:eu-repo/semantics/article, doc-type:Text |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 0884-2914, 2044-5326, 10.1557/jmr.2014.371, info:eu-repo/grantAgreement/Deutsche Forschungsgemeinschaft/SPP 1594/224063632//Spannungs- und Schwingungsrisskorrosion in Zr-basierten massiven metallischen Gläsern |
Page generated in 0.0019 seconds