Cementitious materials will serve as a construction and filler material for the construction of a deep repository of radioactive waste. Therefore, three different materials represented by four samples were studied in the present work. This is CEM II AS 42,5R cement commercially available in Čížkovice, cement CEM III B / 32,5 SV with ash and aggregate used as filler concrete for storage chambers from radioactive waste repository Richard and cement CEM I 42, 5 with fine and coarseraggregate used for fixed radioactive waste (RAW) in Velké Zbytky in the area of ÚJV Řež,as Chemical (silicate analysis) and phase composition (XRD powder diffraction analysis) were determined in the studied materials. Further, the orientation strength of the monolithic samples and their mutual comparison (compression strength measurement) were determined. Percolation leaching experiments were carried out, three columns with CEMII, RICHARD and ÚJV samples were run. The conditions of the experiments were chosen to approach the conditions in the rock environment of a possible deep radioactive waste repository. Synthetic granite water (SGW) was used as the leaching solution. In all column experiments, attempts to observe changesin the concentrations of selectedindicators (Na+ , K+ , OH- ,Ca2+ ,pH, Conductivity, SiO2, Mg2+ and...
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:356495 |
| Date | January 2017 |
| Creators | Podojil, Adam |
| Contributors | Jelínek, Emil, Kozlovcev, Petr |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0022 seconds