Orientadores: Lucia Helena Innocentini Mei, Jose A. M. Agnelli / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-22T10:48:40Z (GMT). No. of bitstreams: 1
Pedroso_AndreaGraf_M.pdf: 2857618 bytes, checksum: 275c6b4baabad74c46e6b1df1d6c519c (MD5)
Previous issue date: 1997 / Resumo: A reciclagem de materiais poliméricos é de fundamental importância devido a fatores ambientais, econômicos e sociais, e nos últimos anos tem crescido de forma extremamente expressiva. A reciclagem mecânica dos materiais termoplásticos causa a decomposição das cadeias poliméricas levando a perda das propriedades mecânicas. Os termoplásticos de engenharia são produtos comerciais com propriedades físicas superiores aos termoplásticos convencionais e apresentam propriedades desejáveis após a reciclagem. Quando os termoplásticos de engenharia são reforçados com fibras de vidro, eles apresentam aumentos substanciais nas propriedades 'mecânicas, as quais são dependentes das distribuições de comprimentos das fibras de vidro. As poliamidas são consideradas os principais termoplásticos de engenharia, porém, sua natureza higroscópica requer alguns cuidados especiais durante o processamento. Rejeitos industriais de poliamida 6 reforçada com fibras de vidro, provenientes de moldagem por injeção, foram reprocessados e as propriedades do material reprocessado foram analisadas através de ensaios físico-mecânicos, análises térmicas, microscopias óptica e eletrônica de varredura. Os resultados obtidos indicaram que o material reprocessado apresentou propriedades tísico-mecânicas satisfatórias, podendo ser usado para várias aplicações onde estas propriedades são desejáveis. O reprocessamento resultou em decréscimos de aproximadamente 16% na resistência à tração e no módulo de flexão, e de 6% para a elongação na ruptura sob tração / Abstract: The recycling of polymeric materiais is of fundamental importance due to environmental, economic, and social aspects, so that in recent years the use of this process is growing significantly. The mechanical recycling of thermoplastic materiais causes the decomposition of polymeric chains leading to mechanical properties loss. The engineering thermoplastics are comercial products with physical properties superior to the conventional thermoplastics and which show specified properties after recycling. When the engineering thermoplastics are reinforced with glass fiber they show a substancial improvement in their mechanical properties, although this properties are dependent on the glass fiber length distribution. The polyamides have been the most widely used engineering thermoplastics, although, their higroscopic nature requires special care during their processing. Industrial wastes of polyamide 6. reinforced with glass fiber, originated from injection molding, were reprocessed and the properties of recycled material were analized through mechanical tests, therma analysis, optical microscopy and scanning eletronic microscopy. The results showed that the recycled material presents satisfactory mechanical properties, so it could be used in many aplications where these properties are required. The recycling process caused the tensile strength and the flexural modulus to decrease about 16% and the elongation at failure to decrease about 6% / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266376 |
| Date | 27 February 1997 |
| Creators | Pedroso, Andrea Graf |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Agnelli, José Augusto Marcondes, Mei, Lúcia Helena Innocentini, 1953-, Rosa, Derval dos Santos, Ravagnani, Sergio Persio |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 92f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds