Title: Structural study of nanocrystalline titanium oxide films and their temperature stability Author: Lea Chlanová Department: Department of Condensed Matter Physics Supervisor: Prof. RNDr. Radomír Kužel, CSc., Department of Condensed Matter Physics Abstract: TiO2 thin films can exhibit photocatalytic activity and photoinduced su- perhydrophilicity depending on crystallinity, phase composition and mi- crostructure. These parameters were studied by X-ray diffraction (XRD) and reflectivity (XRR) for magnetron deposited films - nanocrystalline and amorphous, namely their temperature and time evolution. For nanocrystalline films, it was found that higher partial oxygen pressure during the deposition is beneficial. Small anatase crystallites were stable up to about 450 ◦ C. Depth-profiling XRD of some samples revealed that rutile phase was only present close to the substrate. For amorphous films it was found that the crystallization depends strongly on the film thickness and it is slower for very thin films. Evolution of the intensities of anatase diffraction peaks with annealing time could be described by a modified Avrami equation. XRD profile was relatively narrow from the very be- ginning of crystallization (at about 220 ◦ C), which indicated relatively larger crystallites (> 100 nm), and hence, nanocrystalline films...
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:375102 |
| Date | January 2018 |
| Creators | Chlanová, Lea |
| Contributors | Kužel, Radomír, Čapková, Pavla, Ganev, Nikolaj |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.002 seconds