Previous issue date: 2012-03-30 / The objective of this research is the fabrication of a composite reinforced with dyed sisal fiber and polyester matrix for application in the fields such as, fashion, clothing,
interior textiles; fashion accessories are some of the examples. For the fabrication of the composite, the sisal fibers were subjected to processes such as: chemical treatment with sodium hydroxide (NaOH) in the removal of impurities; bleaching for
removing the yellowish color of the natural fiber and dyeing with direct dyes to confer the colors blue, green and orange. The search for new technologies ecologically correct has become a major concern in recent decades. Studies show that composite
polymer reinforced by natural fibers is suitable for a large number of applications, and its use is advantageous in terms of economic and ecological. The dyed fibers were cut to a length of 30 mm, is used in the confection of webs. For this purpose, a web
preparer by immersion, developed in the Laboratory of Chemical Textile of UFRN. The composite sheets measuring 300 x 300 x3 mm were molded by compression, with unsaturated orthophthalic polyester as matrix, and the samples in sizes 150 x 25
x 3 mm were cut with the aid of a laser machine, to be subjected to traction and flexion. The mechanical properties of traction and flexion in three points were performed in the Laboratory of metal and mechanical tests of Materials Engineering
of UFRN. The resulting samples from the tests were evaluated in scanning electron microscope (SEM) at CTGas RN. On the basis of the analysis of the results from the mechanical tests, it was observed that the composite had good mechanical behavior,
both in traction as in flexion. Furthermore, it was observed that in the water absorption test, the samples had a different percentage among themselves, this occurred due to the variation of density found in the fibre webs. The images of the
SEM showed the failures from the manufacturing process and the adhesion of fibre/matrix. When the samples were prepared with the dyed fibers to be applied in fashion, the results were positive, and it can be concluded that the main objective of
this work was achieved / A busca por novas tecnologias ecologicamente corretas tem se tornado uma grande preocupa??o nas ?ltimas d?cadas. Estudos comprovam que comp?sitos polim?ricos refor?ados por fibras naturais s?o adequadas a um grande n?mero de aplica??es e
seu uso ? vantajoso em termos econ?micos e ecol?gicos. O objetivo desta pesquisa ? a fabrica??o de um comp?sito refor?ado com fibra de sisal tingida e matriz de
poli?ster para aplica??o na moda: vestu?rio, t?xteis lar, acess?rios de moda etc. Para o seu beneficiamento, as fibras de sisal foram submetidas aos diversos processos: tratamento qu?mico com hidr?xido de s?dio (NaOH) na retirada das
impurezas; alvejamento para remo??o da cor amarelada natural da fibra e tingimento com corantes diretos para conferir as cores azul, verde e alaranjado. As fibras tingidas foram cortadas com comprimento de 30 mm e utilizadas na confec??o das
mantas. Para isso utilizou-se um preparador de manta por imers?o, desenvolvido no Laborat?rio de Qu?mico T?xtil da UFRN. Os comp?sitos medindo 300 x 300 x 3 mm foram moldados por compress?o, com poli?ster insaturado ortoft?lico como matriz, e
as amostras nos tamanhos 150 x25 x3 mm foram cortadas com aux?lio de uma m?quina ? laser, para serem submetidas ? an?lise mec?nica de tra??o e flex?o. As propriedades mec?nicas de tra??o e flex?o em tr?s pontos foram realizadas no
Laborat?rio de Metais e Ensaios Mec?nicos de Engenharia de Materiais da UFRN. As amostras resultantes das propriedades mec?nicas foram avaliadas no Microscopio Eletronico de Varredura (MEV) no CTG?s RN. Com base nas an?lises
dos resultados dos ensaios mec?nicos, observou-se que os compositos tiveram bom comportamento mec?nico, tanto na tra??o como na flex?o. Tamb?m observou-se que no ensaio de absor??o de ?gua, as amostras tiveram um percentual diferente
entre si, isso ocorreu devido ? varia??o da densidade encontrada nas mantas. As imagens do MEV mostraram as falhas provenientes do processo de fabrica??o e a ades?o fibra/matriz. Quando foram preparadas as amostras com as fibras tingidas
para serem aplicadas na moda, os resultados foram positivos e pode-se concluir que o objetivo principal do presente trabalho foi atingido
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/15680 |
Date | 30 March 2012 |
Creators | Oliveira, Jos? Orlando de |
Contributors | CPF:18222161415, http://lattes.cnpq.br/8553209522282182, Felipe, Maria Gorete, CPF:19989490449, http://lattes.cnpq.br/3151683042790067, Souza, Roberto Silva de, CPF:44466927472, http://lattes.cnpq.br/4012782800846844, Ladchumananandasivam, Rasiah |
Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Engenharia Mec?nica, UFRN, BR, Tecnologia de Materiais; Projetos Mec?nicos; Termoci?ncias |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 7.4187 seconds