Previous issue date: 2011-08-12 / CNPq / A necessidade de exploração de óleos mais pesados, em poços cada vez mais profundos e em ambientes mais agressivos tem causado falhas dos materiais por corrosão com grandes prejuízos econômicos e ambientais. Portanto este trabalho teve como objetivo avaliar a influência dos parâmetros de soldagem sobre a geometria (razão entre a altura e a largura- R/L), diluição(D), teor de Ferro, %Fe, e consequentemente resistência à corrosão de revestimentos de ligas de Ni (Hastelloy-276) aplicados por soldagem em aços C-Mn. O processo de soldagem utilizado foi ao Arco Submerso utilizando um arame eletrodo de liga de níquel (Ni-Cr-Mo-4) com diâmetro de 1,14 mm, avaliando duas modalidades de corrente, a corrente pulsada e a corrente convencional. Como substrato foi empregado segmentos de um tubo de aço de especificação API 5L Gr B com espessura de 18 mm e diâmetro interno de 290 mm. Para relacionar a influência das variáveis citadas com as respostas desejadas, foi utilizada a técnica de planejamento de
experimentos com aplicação de planejamento fatorial em dois níveis. O planejamento fatorial foi utilizado apenas na etapa das soldagens dos cordões isolados. As etapas subseqüentes foram confeccionar revestimentos planos com três passes de solda e revestimentos circunferenciais com três passes no interior do tubo, com esse girando e a tocha parada, onde foi avaliado principalmente o teor de Fe e resistência à corrosão. Para os cordões isolados na modalidade de corrente pulsada, foram obtidos valores de diluição de 3,6% a 22,26% e valores de R/L de 0,23 a 0,67, sendo o resultado mais satisfatório de 12,76% e 0,28 para D e R/L respectivamente. Para os corões isolados na modalidade de corrente convencional, os valores de diluição variaram de 9,62% a 23,19%, com R/L variando de 0,21 a 0,60, sendo o resultado mais satisfatório de 11,81% e 0,28 para D e R/L. Nos revestimentos com três passes foram alcançados melhores resultados de resistência à corrosão na modalidade de corrente convencional, sendo a variável distância do bico de contato à peça, DBCP, de maior influência nos resultados. / The need for exploration of heavier oils, in ever deeper wells and more aggressive environments has caused failures due to corrosion of materials with large economic and environmental losses. Therefore the aim of this study was to evaluate the influence of welding parameters on geometry (ratio of height to width - R/L), dilution (D), Iron content, % Fe, and hence corrosion resistance of Ni alloy overlays (Hastelloy-276) applied by welding on C-Mn steels. Submerged Arc welding process was used with pulsed and conventional current using nickel alloy wire electrode (Ni-Cr-Mo-4) with 1.14 mm diameter as filler metal. A segments of API 5L Gr B steel pipe with 18 mm thickness and 290 mm internal diameter was used as substrate. To relate the influence of the variables mentioned with the desired responses design of experiments technique with application of factorial design at two levels was used. The factorial design was used only in the stage of isolated welding beads. Subsequent steps consisted of overlay with 3 welding pass in plan position and inside of the pipe in rotation movement with the torch stopped. In this case it was also being evaluated mainly % Fe and corrosion resistance. For isolated beads in the pulsed current mode, dilution values were obtained from 3.6% to 22.26% and values of R / L from 0.23 to 0.67, being the most satisfactory result of 12.76% and 0.28 for
D and R / L respectively. For isolated beads in the conventional current method,dilution values ranged from 9.62% to 23.19%, with R / L ranging from 0.21 to 0.60, being the most satisfactory result of 11.81% and 0.28 for D and R / L. At overlays with three passes, have been achieved better results in the corrosion resistance with conventional current mode, and the variable “distance from the contact tip to the workpiece, DBCP”, had the greatest influence on results.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1832 |
Date | 27 September 2018 |
Creators | BATISTA, Valmir Rodrigues. |
Contributors | MACIEL, Theophilo Moura., CASTRO, Walman Benício de., FERREIRA, Ricardo Artur Sanguinetti., SANTOS, Marco Antonio dos. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Relation | CAPES |
Page generated in 0.0193 seconds