lombardo_ghl_me_sjc.pdf: 2372333 bytes, checksum: 95102ab2066b717f006018fb102db267 (MD5) / Este trabalho avaliou a influência do tratamento superficial do metal (jateamento com óxido de alumínio e ponta de tungstênio), na resistência ao cisalhamento, entre uma liga de Co-Cr (StarLoy C - DeguDent) e duas cerâmicas (StarLight Ceram - DegunDent e Duceram Kiss - Degudent). Foram confeccionados quarenta e oito padrões metálicos de formato cilíndrico, com altura total de 4,7 mm, tendo diâmetro diferenciado entre as extremidades; a maior com 5 mm e a menor com 3,7 mm (ISO 11405), sendo doze para cada grupo: G1- superfície metálica jateada com óxido de alumínio + StarLight Ceram; G2- superfície metálica tratada com ponta de tungstênio + StarLight Ceram; G3- superfície metálica jateada com óxido de alumínio + Duceram Kiss e G4- superfície metálica tratada com ponta de tungstênio + Duceram Kiss. O ensaio de cisalhamento foi realizado em máquina de ensaio universal (Emic DL 1000, São José dos Pinhais, Brasil), com célula de carga de 100 Kg, à velocidade de 0,5 mm/min, utilizando um dispositivo específico (faca com entalhe). Após o ensaio, foi realizada a análise fractográfia e os dados obtidos analisados estatisticamente pelo teste ANOVA (2 fatores). Foram observados os seguintes valores médios de resistência de união: G1 (57,97l11,34 MPa); G2 (40,62l12,96 MPa); G3 (47,09l13,19 MPa) e G4 (36,80l8,86 MPa). Concluiu-se que o tratamento superficial com óxido de alumínio, aumentou a resistência de união entre metal e cerâmica, independente do tipo de cerâmica utilizada. / The aim of this study was to evaluate the influence of the surface treatment (sandblasting with aluminium oxide and tungsten carbide bur), on the shear bond strength among a Co-Cr alloy (StarLoy C - DeguDent) and two ceramics (StarLight Ceram - DeguDent and Duceram Kiss - Degudent). Forty eigth metal cilindric specimens were made with 4,7 mm high, with two different diameters: one with 5,5 mm and the other with 3,7 mm (ISO 11405), with twelve specimens for each one of the four groups: G1 - sandblasting + StarLigth Ceram; G2 - tungsten carbide burs + StarLigth Ceram; G3 - sandblasting + Duceram Kiss and G4 - tungsten carbide burs + Duceram Kiss. The shear test was made with a universal testing machine (Emic DL 1000, São José dos Pinhais, Brazil), with load of 100 kg, with the crosshead speed of 0,5 mm/min, using a specific device (knife with an indent - Ultradent). The fracture analysis of the surfaces was made and the data were statistically analyzed with the ANOVA (two way). The means and the standard deviations of the shear bond strength were: G1 (57,97l11,34 MPa); G2 (40,62l12,9 MPa); G3 (47,09l13,19 MPa) e G4 (36,80l8,86 MPa). It could be concluded that the surface treatment with the tungsten carbide bur reduced the shear bond strength, independent of the ceramics used.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/95443 |
| Date | 24 July 2007 |
| Creators | Lombardo, Geraldo Henrique Leão [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Nishioka, Renato Sussumu [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 108 f. : il. anexo |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.0027 seconds