Previous issue date: 2018-02-23 / Avaliar in vitro a influência dos diferentes tempos de condicionamento do ácido
metafosfórico 40% e ácido ortofosfórico 37% em diferentes viscosidades nas
propriedades adesivas da interface radicular. As raízes de 72 pré-molares inferiores
uniradiculares foram preparadas, tratadas endodonticamente e distribuídas
aleatoriamente em 8 condições experimentais (n=9) de acordo com a combinação das
variáveis: Ácido [ácido ortofosfórico 37% (AOF) e ácido metafosfórico 40% (AMF)],
viscosidade do ácido [(gel (G) e líquido (L)] e tempos de aplicação (7 e 15 s). Sessenta
e quatro raízes foram cimentadas com sistema adesivo Ambar Universal e o cimento
dual Allcem Core. Após a cimentação, os dentes foram seccionados transversalmente
em fatias e submetidas ao teste de resistência de união por Push-out (RU) (n=6). Para
o teste de nanoinfiltração (NI), fatias de cada grupo foram imersas em solução de nitrato
de prata para análise por Microscopia eletrônica de varredura (MEV). Para análise
morfológica da superfície radicular, os dentes que não foram cimentados (n=8), foram
aleatoriamente alocados de acordo a cada condição experimental e analisados por
MEV após condicionamento. Os dados de RU e NI foram submetidos a ANOVA 3
fatores e teste de Tukey (α=0,05). O AMF apresentou valores de RU similares ao AOF
independente do tempo e da viscosidade utilizada (p>0,001). O aumento do tempo,
aumentou significativamente os valores de RU (p<0,001). AOF apresentou maiores
valores de NI quando comparado com AMF (p<0,001). Quando foi comparada a
viscosidade, independente do tipo de ácido utilizado, o ácido liquido aumentou
significativamente a deposição de NI (p<0,05). O incremento do tempo de aplicação do
AOF resultou em um significativo aumento de NI (p<0,01). O AMF 40% apresentou RU
similar quando comparado ao AOF 37%, independente da viscosidade e tempo de
aplicação com uma menor NI. / In-vitro evaluation the influence of the different conditioner times (7 and 15 seconds) of
40% meta-phosphoric acid (MPA) and 37% ortho-phosphoric acid (OPA) in different
viscosities (gel and liquid) on the adhesive properties of the root interface. Seventy-two
roots of human premolars were endodontically prepared and randomly assigned into the
8 experimental conditions (n = 9) according to the combination of the variables: Acid
[37% ortho-phosphoric acid (OPA) and 40 meta-phosphoric acid (MPA)]; acid viscosity
[(gel (G) and liquid (L)]; and application times (7 and 15 s). The adhesive system Ambar
Universal was applied and the fiber post were cemented with dual cement Allcem Core.
After cementation, the teeth were cross-sectioned into slices and subjected to the pushout
bond strength test (BS) (n = 6) at a speed (0.5 mm/min). For the nanoleakage (NL)
evaluation, slices was randomly selected from each group and were immersed in silver
nitrate solution for analysis by Scanning Electron Microscopy (SEM). For morphological
analysis of the root surface, the teeth that were not cemented (n = 8) were randomly
allocated according to each experimental condition and analyzed by SEM after acid
etching. Data from BS and NL were submitted to ANOVA 3 factors and Tukey's test (
= 0.05). MPA showed similar values of BS to OPA, regardless of the application time
and viscosity used (p < 0.001). The increase of application time resulted in a statistically
higher BS values (p < 0.001). OPA increased the values of NL when compared with
MPA (p < 0.001). When the viscosity was compared, regardless of the acid used, the
liquid acid promoted a significant increase in the silver nitrate. (p < 0.05). The increase
of the time of application of the OPA resulted in a significant increase of NL (p < 0.01).
The use of 40% MPA promoted a similar BS, regardless of the viscosity and application
time with lower NL than the 37% OPA.
Identifer | oai:union.ndltd.org:IBICT/oai:tede2.uepg.br:prefix/2481 |
Date | 23 February 2018 |
Creators | Ocampo, Jessica Bedoya |
Contributors | Loguercio, Alessandro Dourado, Cardenas, Andrés Felipe Millan, Siqueira, Fabiana Suelen Figuerêdo, Bauer, José Roberto de Oliveira, Siqueira, Márcia Fernanda de Rezende |
Publisher | Universidade Estadual de Ponta Grossa, Programa de Pós-Graduação em Odontologia, UEPG, Brasil, Departamento de Odontologia |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Biblioteca Digital de Teses e Dissertações da UEPG, instname:Universidade Estadual de Ponta Grossa, instacron:UEPG |