Orientador: Luis Alexandre Maffei Sartini Paulillo / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-25T22:01:08Z (GMT). No. of bitstreams: 1
Prieto_LuciaTrazzi_D.pdf: 2940883 bytes, checksum: c9367f60f0af737b2b46e381a5ba5b3d (MD5)
Previous issue date: 2014 / Resumo: O objetivo deste estudo "in vitro" foi avaliar as propriedades físicas e químicas de cimentos resinosos e resinas compostas de baixa viscosidade usados na cimentação de facetas laminadas, através da estabilidade de cor e resistência à união após envelhecimento e grau de conversão. Para isso foram utilizados 96 incisivos humanos extraídos divididos, aleatoriamente, em 6 grupos experimentais (n=8), formados pelos sistemas de fixação RelyX Veneer/ Single Bond 2 (3M ESPE), RelyX ARC/Single Bond 2 (3M ESPE), Filtek Z350 XT Flowable/Single Bond 2 (3M ESPE), Variolink Veneer/Tetric N-Bond (Ivoclar-Vivadent), Variolink II/ Tetric N-Bond (Ivoclar-Vivadent) e Tetric N-Flow/ Tetric N-Bond (Ivoclar-Vivadent), utilizados na cor A1. Para se avaliar a estabilidade de cor foram realizados desgastes com máquina de preparo na face vestibular de 0,6 mm de profundidade simulando preparos para facetas laminadas em 48 incisivos humanos e foram confeccionadas facetas laminadas em cerâmica IPS Empress Esthetic que foram cimentadas de acordo com os grupos experimentais. Vinte e quatro horas após a cimentação a cor inicial foi avaliada com o auxílio de espectrofotômetro (Easyshade-Vita). Após o envelhecimento acelerado por luz UV-B durante 300 horas (150Kj/m), nova mensuração de cor foi realizada. A avaliação da resistência ao microcisalhamento foi realizada selecionando outros 48 incisivos humanos (n=8) que receberam a cimentação de dois cilindros cerâmicos (IPS Empress Esthetic) (1 x 2 mm) sobre a face vestibular planificada, após vinte e quatro horas o primeiro cilindro foi acoplado à maquina EZ-test para o teste de resistência e o cilindro remanescente foi submetido ao envelhecimento acelerado por luz, e novo ensaio de resistência à união realizado, avaliando-se também o padrão de fratura em microscópio óptico. Para avaliação do grau de conversão foram confeccionados 60 espécimes (n=10) de cada material resinoso (5 x 0,5 mm) e os espectros de absorção foram obtidos através do espectrômetro Spectrum 100 FTIR/UATR. Os dados foram submetidos a Análise de Variância e teste de Tukey ('alfa'=0,05). Em relação a estabilidade de cor todos os materiais testados apresentaram grande alteração de cor perceptível clinicamente ('delta'E>3.3), porém não apresentaram diferença estatísticas entre si. Para a resistência à união os sistemas de fixação Single Bond 2/RelyX ARC e Tetric N-Bond/Variolink II apresentaram os melhores valores quando comparados aos demais sistemas, Tetric N-Bond/Variolink Veneer e Single Bond 2/ RelyX Veneer foram semelhantes entre si e superiores as resinas compostas de baixa viscosidade, que apresentaram os valores mais baixos. Em relação ao padrão de fratura os cimentos duais apresentaram maior porcentagem de fraturas do tipo coesiva em cerâmica (62,5%) enquanto os cimentos fotoativados e resinas de baixa viscosidade obtiveram maior porcentagem de falhas do tipo adesiva (50 a 75%). Quanto ao grau de conversão, RelyX ARC apresentou o melhor resultado, sendo que Variolink II, RelyX Veneer e Filtek Flow apresentaram resultados intermediários com diferenças estatísticas entre si e Tetric Flow e Variolink Veneer apresentaram o menor grau de conversão. Baseando-se nos resultados pôde-se concluir que os sistemas de fixação mostraram grande alteração de cor após o envelhecimento, em relação ao teste de microcisalhamento e grau de conversão os materiais duais obtiveram melhor desempenho quando comparados aos outros materiais testados. / Abstract: The aim of this " in vitro " study was to evaluate the chemical and physical properties of different resin cements and flowable resin composites used to lute veneers on enamel by color stability and bond strength submitted to accelerated artificial aging, and degree of conversion. Ninety-six extracted human incisors were randomly divided into 6 experimental groups (n = 8), according to the different luting systems evaluated: RelyX Veneer / Single Bond 2 (3M ESPE), RelyX ARC / Single Bond 2 (3M ESPE), Filtek Z350 XT Flowable/ Single Bond 2 (3M ESPE), Variolink Veneer / Tetric N - Bond (Ivoclar Vivadent), Variolink II / Tetric N - Bond (Ivoclar Vivadent) and Tetric N -Flow / Tetric N - Bond (Ivoclar Vivadent), used shade A1. To evaluate the color stability, wears of 0.6 mm thick were performed on labial surface to simulate veneer preparations. Forty-eight IPS Empress Esthetic veneers were cemented according to the experimental groups evaluated. Twenty-four hours after luting procedures the initial color was measured with spectrophotometry (Easyshade-Vita). After accelerated aging by UV-B light for 300 hours (150Kj/min), final color readout was measured. To evaluate the microshear bond strength another 48 human incisors was selected. Two ceramic cylinders (IPS Empress Esthetic) (d=1 mm x 2 mm thick) were lute on the labial enamel surface previous prepared as described before. After twenty-four hours, the first cylinder was coupled to the EZ -test machine for measuring the initial bond strength and, the remaining cylinder was submitted to accelerated artificial aging by light, and before bond strength test. Fracture pattern was analyzed under light microscope. To evaluate the degree of conversion 60 specimens (n=10) of each resin material (5x0.5 mm) were obtained and Fourier transform infrared spectroscopy (FTIR) was used to evaluate the absorption spectra. The data were submitted to ANOVA and Tukey test ('alfa'= 0.05). There was clinically perceptible color change ('delta'E > 3.3) for all materials tested; there were no statistical difference among the color stability of any luting materials. For bond strength test the luting systems single Bond2/ RelyX ARC and Tetric N-Bond/Variolink II showed the highest values when compared to others systems, Tetric N-Bond/Variolink Veneer and Single Bond 2/RelyX Veneer were similar between and superior to flowable resin composites, which showed lowest values. Regarding fracture pattern the dual cured resin cements showed a higher percentage of cohesive fracture patterns on ceramic (62.5%) and the light-cured resin cement and the flowable resin composites, adhesive fracture pattern (50-75%). For the degree of conversion, the following decreasing sequence was found: RelyX ARC>Variolink II>RelyX Veneer>Filtek Z350 XT Flowable>Tetric Flow>Variolink Veneer. For the microshear bond strength Single Bond 2/RelyX ARC=Tetric N-Bond/Variolink II =Tetric N-Bond/Variolink Veneer+Single Bond2/RelyX Veneer >flowable resin composite. Based on the results it was concluded that the luting systems showed great after artificial aging, in relation to microshear bond strength test and the degree of conversion of the dual-cured resin cements obtained better performance compared to light-cured resin materials tested / Doutorado / Dentística / Doutora em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289629 |
| Date | 25 August 2018 |
| Creators | Prieto, Lúcia Trazzi, 1984- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Paulillo, Luis Alexandre Maffei Sartini, 1962-, Araújo, Cíntia Tereza Pimenta de, Bueno, Vanessa Castro Pestana da Silveira, Miranda, Diogo de Azevêdo, Baron, Giselle Maria Marchi |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 41 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds