Orientador: Rafael Leonardo Xediek Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T14:20:39Z (GMT). No. of bitstreams: 1
BarrientosNava_JuanRene_M.pdf: 979069 bytes, checksum: 74108d8d78e414edaddbf2d5747d4ee6 (MD5)
Previous issue date: 2015 / Resumo: O objetivo neste estudo foi avaliar a resistência da união ao cisalhamento de cimentos resinosos fotoativados através de diferentes espessuras de cerâmica e o modo de fratura. Foram utilizados os cimentos resinosos RelyX U200 (3M ESPE) e Variolink II (Ivoclar-Vivadent). Sessenta discos de cerâmica IPS Empress Esthetic (Ivoclar-Vivadent) com 12mm de diâmetro foram separados em grupos (n=10) segundo a espessura (0,7; 1,4 e 2,0mm). A superfície dos discos foi condicionada com ácido hidrofluorídrico a 10% por 60s, lavada e seca com jato de ar por 60s. A seguir foi feita aplicação de agente silano por 60s. Uma matriz de elastômero com forma de disco com 15mm de diâmetro e 0,5mm de espessura com quatro orifícios de 1,5mm de diâmetro foi usada para delimitar a área de adesão na cerâmica. A manipulação dos cimentos resinosos foi de acordo com as instruções dos fabricantes, o material inserido nos orifícios da matriz, recoberto com tira de poliéster e lâmina de microscópio com pressão digital. A fotoativação foi realizada através do disco de cerâmica com Ultra Lume LED 5 (Ultradent) com potência de 1200 mW/cm² por 60s. Após armazenagem por 24h em água destilada a 37ºC, os corpos-de-prova foram avaliados com lupa estereoscópica para descartar aqueles com imperfeições. O teste de resistência ao cisalhamento foi conduzido em máquina de Ensaio Universal Instron (Canton, MA, USA), com velocidade de 1 mm/min e com célula de carga de 50Kg até fratura e os valores de resistência da união calculados em MPa. O modo de fratura foi analisado com lupa estereoscópica (LABOMED, Barueri, SP), com aumento de 10 vezes. Os resultados foram submetidos à análise de variância de dois fatores e teste de Tukey (5%). Os modos de fratura foram considerados em função da predominância das falhas sendo a falha coesiva em cerâmica a que prevaleceu. Os resultados mostraram que a interação entre os fatores espessura da cerâmica e cimento, e o fator espessura não foram significantes (p=0,541 e p=0,643, respectivamente), enquanto o fator cimento foi significativo (p=0,009). Pode-se concluir que o cimento Variolink II apresentou resistência de união significantemente maior que a do cimento RelyX U200 / Abstract: The aim of this study was to evaluate the bond shear strength of resin cements photoactivated through different thicknesses of ceramics and the failure mode. RelyX U200 (3M ESPE) and Variolink II (Ivoclar Vivadent) resin cements were used. Sixty ceramic discs of Esthetic IPS Empress (Ivoclar-Vivadent) with 12mm diameter were divided into groups (n=10) according to their thickness (0.7; 1.4 and 2.0mm). The grounded surface was etched with 10% hydrofluoric acid for 60 seconds, rinsed and dried with compressed air for 60s. The following silane application was made for 60s. An elastomeric matrix having 15mm in diameter and 0.5mm in thickness with four holes (1.5mm in diameter) was used to define the adhesion area in the ceramic. The manipulation of the resin cements was carried out according to the manufacturers¿ instructions and inserted into the holes of the elastomer matrix, covered with plastic strip and finger pressed with a microscope slide. Light curing through ceramic was Ultra Lume LED 5 (Ultradent) with power 1200mW/cm² for 60s. After storage for 24h in distilled water at 37ºC, all resin cylinders were checked under magnification. The shear strength test was conducted in a Instron Universal Testing Machine, at cross-head speed of 1mm/min with load of 50Kg until fracture. The bond strength values were calculated (MPa). The fracture mode was analyzed using stereoscopic lens 10x (LABOMED, Barueri, SP). The results were submitted to two-way ANOVA and the means compared by Tukey¿s test (5%). Cohesive failure mode within ceramic was predominant. The results showed that the interaction between the factors and cement thickness, and the thickness factor were not statistically significant (p=0.541 and p=0.643, respectively). The cement factor was significant (p=0.009). In conclusion, the Variolink II showed significantly higher bond strength value than the RelyX U200 cement / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288537 |
| Date | 04 June 2015 |
| Creators | Barrientos Nava, Juan Rene, 1972- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Rafael Leonardo Xediek, 1974-, Montagner, Antonio Marcos, Correr, Ana Rosa Costa |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 28 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds