In the study, conductive distributed Bragg reflectors (DBRs) fabricated at room temperature based on porous indium tin oxide (ITO) on dense ITO bilayers were proposed for resonant cavity organic light emitting diodes (RCOLEDs). In the fabrication of the ITO DBRs, the low refractive index porous ITO films were obtained by applying supercritical CO2 treatment at different temperature and pressures on the spin-coated sol-gel ITO films. On the other hand, the high refractive index ITO films were grown at room temperature by long-throw reactive ratio-frequency magnetron sputtering. The refractive index of the porous ITO film and ITO films were 1.54 and 2.0, respectively. For the DBR with 4 pairs ITO bilayers, the optical reflectance of more than 70 % was achieved. The stop band and the average resistivity is 140 nm and 2.2¡Ñ10-3 £[-cm, respectively. Finally, electrical and optical characteristics of the RCOLEDs fabricated on the ITO DBR were investigated and compared with those of the conventional OLEDs. The maximum luminous efficiency of 3.79 cd/A was obtained at 347 mA/cm2 for the RCOLED. This luminous efficiency was 26 % higher than that of the conventional OLED.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0628112-130754 |
| Date | 28 June 2012 |
| Creators | Chuang, Tung-Lin |
| Contributors | Wen-Yao Huang, Ann-Kuo Chu, Ting-Chang Chuang, Yi-Jen Chiu |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0628112-130754 |
| Rights | user_define, Copyright information available at source archive |
Page generated in 0.0015 seconds