The armchair variety of single-wall carbon nanotubes (SWCNTs) is the only nanotube species that behaves as a metal with no electronic band gap and massless carriers, making them ideally suited to probe fundamental questions of many-body physics of one-dimensional conductors as well as to serve in applications such as high-current power transmission cables. However, current methods of nanotube synthesis produce bulk material comprising of a mixture of nanotube lengths, diameters, wrapping angles, and electronic types due to the inability to control the growth process at the nanometer level. As a result, measurements of as-grown SWCNTs produce a superposition of electrical and optical responses from multiple SWCNT species.
This thesis demonstrates production of aqueous suspensions composed almost entirely of armchair SWCNTs using a post-synthesis separation method employing density gradient ultracentrifugation (DGU) to separate different SWCNT types based on their mass density and surfactant-specific interactions. Resonant Raman spectroscopy determines the relative abundances of each nanotube species, before and after DGU, by measuring the integrated intensity of the radial breathing mode, the diameter-dependent radial vibration of the SWCNT perpendicular to its main axis, and quantifies the degree of enrichment of bulk nanotube samples to exclusively armchair tubes. Raman spectroscopy of armchair-enriched samples of the G-band mode, which is composed of longitudinal (G-) and circumferential (G+) vibrations oscillating parallel and perpendicular to the tube axis, shows that the G- peak, long-held to be an indicator for the presence of metallic SWCNTs, appears only when electronic resonance with narrow-gap semiconducting SWCNTs occurs and shows only the G+ component in spectra containing only armchair species. Finally, by combining optical absorption measurements with nanotube composition as determined earlier via Raman scattering, peak fitting of absorption spectra indicates that interband transitions of armchair SWCNTs are strongly excitonic as shown by the highly symmetric peak lineshapes, a property normally attributed to semiconductors. Such lineshapes allow classification of armchair SWCNTs as a unique hybrid class of optical nanomaterial. Combining absorption and Raman scattering measurements establishes a distinct optical signature that describes the fundamental optical processes within armchair SWCNTs and lays the foundation for future studies of many-body photophysics and electrical applications.
| Identifer | oai:union.ndltd.org:RICE/oai:scholarship.rice.edu:1911/71962 |
| Date | 16 September 2013 |
| Creators | Haroz, Erik |
| Contributors | Tittel, Frank K. |
| Source Sets | Rice University |
| Language | English |
| Detected Language | English |
| Type | thesis, text |
| Format | application/pdf |
Page generated in 0.0238 seconds