ribeiro_r_me_ilha.pdf: 2200003 bytes, checksum: ed990be7049f27e3065183a9019db48f (MD5) / O presente trabalho utiliza o processo de soldagem por eletrodo revestido, para a aplicação de revestimentos metálicos que aumentam a resistência ao desgaste de peças submetidas a abrasão, utilizados na indústria sucroalcooleira. Como metal de revestimento foi utilizado eletrodo do tipo Fe-Cr-C, e como metal de base um aço estrutural ASTM A-36. Realizou-se um estudo sobre a influência dos parâmetros de soldagem, principalmente a corrente de soldagem, nas características da dureza, diluição, geometria do cordão e microestrutura, visando maximizar a resistência ao desgaste por abrasão à baixa tensão obtida pelo ensaio de roda de borracha definido pela norma ASTM G-65-91. Para a otimização das condições de soldagem foi utilizado um planejamento experimental, proporcionando uma ampla faixa de depósitos com características diferentes e conseqüente variação na resistência ao desgaste. Dos resultados obtidos ficou evidenciada a influência dos parâmetros de soldagem na resistência a abrasão à baixa tensão, assim como uma certa correlação entre dureza e resistência ao desgaste. A diluição mostrou-se influente na formação da microestrutura do revestimento, sendo que aqueles que apresentaram uma maior quantidade de carbonetos primários demonstraram melhor resistência ao desgaste do que os revestimentos com carbonetos secundários. / The application of shielded metal arc welding process for hardfacing aiming the enhance of wear resistance, applied in sugar and alcohol industries, is presented in this work. The consumable was Fe-Cr-C, and the base plate is a structural steel ASTM A-36. The influence of the welding process variables such as: current, voltage and travel speed were evaluated and related to its influence on the characteristics of the hardness dilution, bead dimension and microstructure of hardfacing. The aim was to maximize the low stress abrasion resistance obtained by the standard test ASTM G-65-91. To optimize the welding conditions, an experimental design was applied to obtain a wide range of weld deposits with different characteristics and wear resistances. There was evidence of the influence of the welding process variables in the abrasion resistance and some relation between the hardness and wear resistance. The dilution influenced the microstructure of the hardfacing for all weld deposits; those with higher primary carbides contents had performance better than those with secondary carbides under low stress abrasion test conditions.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/90838 |
Date | 26 November 2004 |
Creators | Ribeiro, Rubens [UNESP] |
Contributors | Universidade Estadual Paulista (UNESP), Ventrella, Vicente Afonso [UNESP] |
Publisher | Universidade Estadual Paulista (UNESP) |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | xviii, 104 f. : il. |
Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
Rights | info:eu-repo/semantics/openAccess |
Relation | -1, -1 |
Page generated in 0.0016 seconds