In this study, highly C-axis oriented AlN thin films stacked upon Al bottom electrode on Si and Glass substrate are deposited with Reactive RF magnetron sputtering Technique. Three different sputtering systems were utilized to evaluate the optimized growth parameters. Room temperature growth was applied to the all system. During thin film growing , the substrate bias condition, sputtering work pressure, sputtering power and the N2 concentration are those key parameters to be adjusted in order to gain smooth surface morphology and highly C-axis prefer orientation AlN thin films.
The crystallography of the deposited films was analyzed by x-ray diffraction (XRD). Film surface morphology was characterized by scanning electron microscopy (SEM). Meanwhile, transmission electron microscopy (TEM) was adopted to observe the microstructure and determine the grain size of the film.
The results of the XRD patterns showed that in a 17cm long sputtering working distance condition, the AlN (002) can be obtained and the peak intensity can be increased when the sputtering power was fixed meanwhile reduced the working pressure and applied the negative bias on the substrate. The surface morphology can be improved with long working sputtering distance. The micrography of the TEM reveals that there is a transition region between Al metal and AlN film. Fine column structures can be observed in the initial growth stage. The size of the grain increased as the film became thicker. Strong AlN (002) ring pattern was obtained from the region of the top of the film. It indicates that the AlN (002) will not appear till the thickness of the film reach the critical thickness.
Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0515100-125959 |
Date | 15 May 2000 |
Creators | Huang, Ching-Ju |
Contributors | Li-Wei Tu, K.Y. Hsieh, S.L. Huang |
Publisher | NSYSU |
Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
Language | Cholon |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0515100-125959 |
Rights | unrestricted, Copyright information available at source archive |
Page generated in 0.0009 seconds