Previous issue date: 1995-12-18 / CNPq / Esta dissertação apresenta os resultados de uma pesquisa desenvolvida com o objetivo de se utilizar o agregado graúdo não convencional calcário, de formações calcítica e dolomítica, como agregado alternativo em substituição ao agregado convencionalmente usado na fabricação dos concretos betuminosos usinados à quente, como forma de redução de custos de obras rodoviárias, em regiões onde as rochas calcárias são predominantes. Para que pudessem ser comprovadas as características que mostram
a resistência da mistura betuminosa, foi utilizado o Ensaio Marshall. Foram feitos ensaios físicos e mecânicos de forma a comprovar suas características na pavimentação. São
apresentados alguns resultados de serviços executados na pavimentação da cidade de Mossoró-RN, com resultados satisfatórios de uso nas diferentes camadas do pavimento.
Os resultados obtidos nesta pesquisa permitiram concluir que devido a resistência satisfatória e propriedades similares as da brita granítica além de menores custos de extração e britagem, o agregado calcário pode substituí-la com muita propriedade, quando empregado no uso de concreto betuminoso usinado à quente como revestimento em rodovias, reduzindo-se o custo final da obra. / This thesis presents the results of an investigation carried out to study the performance of a non conventional aggregate, calcareous aggregate of the dolomitic and calcitic formation, in substitution to the dolomitic and calcitic aggregate. used to fabricate hot-mix bituminous concrete. The predominant characteristics of the bituminous mixtures were evaluated using the traditional Marshall test. In order to determine the quality of the mixture, physic and mechanic tests were applied. The results obtained in this investigation in regard to existing pavement, named airport of Mossoró-RN city, constructed with calcareous aggregate in the bituminous mixtures, revealed that the altermative mixture made with calcareous aggregate, is a valid one. Also, the results from laboratory tests, showed that the strength property of the bituminous mixture made with the normal granitic
aggregate. Therefore, based on these results, it can concluded that the calcareous aggregate is an alternative aggregate that can be used to fabricate bituminous mixtures, in replacement of the conventional granitic aggregate.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/2158 |
| Date | 09 November 2018 |
| Creators | COÊLHO, Rosa Maria Gonçalves. |
| Contributors | CARVALHO, João Batista Queiroz de., BRASILEIRO, Francisco Edmar., LUCENA, Francisco Barbosa de., SANTOS, Sebastião Batista dos. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA CIVIL E AMBIENTAL, UFCG, Brasil, Centro de Tecnologia e Recursos Naturais - CTRN |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds