The objective of this study was to compare the time to final set and compressive strength of the white mineral trioxide aggregate (MTA) formulation to the original grey MTA. To test compressive strength, each MTA formulation was placed into Teflon split molds for four hours at 37° Celsius (C) and 100% humidity. Compressive strength of both MTA formulations was measured at 24 hours (n=12) and 21 days (n=19) using an Instron Testing Machine. For determination of time to final set, each MTA formulation (n=6) was placed into a metal mold and maintained at 37° C and 100% humidity while setting. At five-minute time intervals, an indenter needle was lowered onto the surface of the MTA material and allowed to remain in place for five seconds before it was removed from the specimen surface. This process was repeated until the needle failed to make a complete circular indentation in the MTA specimen. Results of a two-way ANOVA indicate that white MTA had a significantly higher compressive strength (mean=32.7 MPa) than grey MTA (mean=25.2 MPa) at 24 hours and no statistically significant differences at 21 days (white mean=38.6 MPa and grey mean=38.0 MPa). Using one-way ANOVA, results indicate that grey MTA had a significantly longer time to final setting time (mean=296 min) compared to white MTA (mean=276 min). Based on this study, the results suggest that white MTA is an effective substitute for grey MTA.
| Identifer | oai:union.ndltd.org:vcu.edu/oai:scholarscompass.vcu.edu:etd-1646 |
| Date | 01 January 2004 |
| Creators | Spencer, David Lowell |
| Publisher | VCU Scholars Compass |
| Source Sets | Virginia Commonwealth University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
| Rights | © The Author |
Page generated in 0.0022 seconds