Kinetics and thermodynamics of bismuth (Bi) underpotential deposition (UPD) on ruthenium (Ru) and on electrochemically formed Ru oxide are studied using electrochemical quartz crystal microbalance technique. The Bi UPD and Bi bulk deposition are observed both on Ru and on electrochemically formed Ru oxide electrodes. The anodic peak potential of Bi UPD shifts slightly to positive potential as the scan rate increases. The peak current ratio (IAnode/ICathode) of Bi UPD and Bi bulk increases as the scan rate increases. Bi monolayer coverage calculated from mass (MLMass) and from charge (MLCharge) with scan rates dependent are compared both in Bi UPD region and in Bi bulk region. Stability and oxidation time effects are also investigated. Bi UPD on Ru and on electrochemically formed Ru oxide are quasi-reversible, scan rate independent, oxidation time dependent, and have higher plating efficiency on Ru. However, Bi bulk deposition on Ru and on electrochemically formed Ru oxide are quasi-reversible, scan rate dependent, oxidation time independent, and have higher plating efficiency on electrochemically formed Ru oxide. Both Bi UPD adatoms and Bi bulk are unstable in 0.5M H2SO4.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc103354 |
| Date | 12 1900 |
| Creators | Lin, Po-Fu |
| Contributors | Chyan, Oliver M. R., Petros, Robby A. |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Public, Lin, Po-Fu, Copyright, Copyright is held by the author, unless otherwise noted. All rights Reserved. |
Page generated in 0.0017 seconds