The erosion or dissolution of stainless steel grade 304 as base metal by molten brazing fillermetal was investigated using one nickel and two iron based filler metals. The difference betweentwo iron filler metal is 5 % Manganese content in one of the filler metal. The Wettability of fillermetal is effected by oxidation of base or filler metal for which high vacuum or non reacting gasis used as a furnace atmosphere to reduce the partial pressure of oxygen. The furnace parameterseffecting erosion of base metal was observed e.g. peak temperature and brazing time. The effectof filler mass was also observed. The erosion depth was measured by light optical microscope.All the three filler metal shows different erosion behavior in nitrogen atmosphere compare tohigh vacuum. In high vacuum some of the elements evaporates at brazing temperature whichchanges the properties of filler metal. This change of composition in filler metal was observed byEDX analysis. SEM analysis was used to identify different element rich phases.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-116688 |
Date | January 2012 |
Creators | jahanzeb, Nabeel |
Publisher | KTH, Materialvetenskap |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds