Graphene has attracted significant research attention for next generation of semiconductor devices due to its high electron mobility and compatibility with planar semiconductor processing. In this dissertation, the influences of Ohmic metals and high dielectric (high-k) constant aluminum oxide (Al2O3) deposition on the structural and electrical properties of multi-layer epitaxial graphene (MLG) grown by graphitization of silicon carbide (SiC) substrates have been investigated. Uniform MLG was successfully grown by sublimation of silicon from epitaxy-ready, Si and C terminated, 6H-SiC wafers in high-vacuum and argon atmosphere. The graphene formation was accompanied by a significant enhancement of Ohmic behavior, and, was found to be sensitive to the temperature ramp-up rate and annealing time. High-resolution transmission electron microscopy (HRTEM) showed that the interface between the metal and SiC remained sharp and free of macroscopic defects even after 30 min, 1430 °C anneals. The impact of high dielectric constant Al2O3 and its deposition by radio frequency (RF) magnetron sputtering on the structural and electrical properties of MLG is discussed. HRTEM analysis confirms that the Al2O3/MLG interface is relatively sharp and that thickness approximation of the MLG using angle resolved X-ray photoelectron spectroscopy (ARXPS) as well as variable-angle spectroscopic ellipsometry (VASE) is accurate. The totality of results indicate that ARXPS can be used as a nondestructive tool to measure the thickness of MLG, and that RF sputtered Al2O3 can be used as a (high-k) constant gate oxide in multilayer grapheme based transistor applications.
Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc68009 |
Date | 05 1900 |
Creators | Maneshian, Mohammad Hassan |
Contributors | Shepherd, Nigel, Srivilliputhur, Srinivasan, Reidy, Rick, Du, Jincheng, Bouanani, Mohammed El |
Publisher | University of North Texas |
Source Sets | University of North Texas |
Language | English |
Detected Language | English |
Type | Thesis or Dissertation |
Format | Text |
Rights | Public, Copyright, Maneshian, Mohammad Hassan, Copyright is held by the author, unless otherwise noted. All rights reserved. |