Two types of Mo₂C have been investigated: polycrystalline β-Mo₂C and single crystal α-Mo₂C. The β-Mo₂C material was synthesized via a temperature-programmed method, and then characterized using x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS), CO chemisorption, and N₂ physisorption. The catalytic activity of the β-Mo₂C was tested for cumene hydrogenation under high pressure conditions, and the effect of sulfur and oxygen poisons on cumene hydrogenation was also investigated.
As a complement to the work done on polycrystalline β-Mo₂C, UHV studies of single crystal α-Mo₂C were undertaken to provide fundamental information about a well-characterized Mo₂C surface. The (0001) surface of α-Mo₂C was investigated using XPS and low energy electron diffraction (LEED). It was found that an ion-bombarded surface could be prepared as either Mo-terminated or C-terminated by choosing either low annealing temperatures (~1000 K) or high annealing temperatures (~1500 K), respectively. CO and O₂ adsorption was also studied on α-Mo₂C (0001) using thermal desorption spectroscopy (TDS), XPS, Auger electron spectroscopy (AES), and LEED. Finally, thiophene adsorption was investigated on α-Mo₂C (0001). / Ph. D.
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/40502 |
| Date | 23 June 1998 |
| Creators | St. Clair, Todd P. |
| Contributors | Chemical Engineering, Cox, David F., Hochella, Michael F. Jr., Dillard, John G., Hanson, Brian E., Oyama, Shigeo Ted |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Detected Language | English |
| Type | Dissertation |
| Format | application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | diss.PDF |
Page generated in 0.0126 seconds