High fuel utilization SOFCs could eliminate emissions from systems that include afterburners and potentially be suitable for carbon sequestration, while producing electricity more efficiently. Current fuel utilization operating points are typically chosen at approximately 85% for Ni-cermet anodes because higher fuel utilization frequently results in the formation of nickel oxide and reduces drastically the performance of the SOFC. In this work the feasibility of an in-plane graded anode architecture with a transition from a material with high catalytic activity to materials more stable under high fuel utilization conditions was evaluated through a steady-state SOFC finite element model. Thereafter, plasma spraying of solution precursor feedstock (SPPS) and suspension feedstock (SPS) was used to fabricate ceramic coatings that could potentially be used as SOFC anodes for high fuel utilization conditions. Microstructural, electrical and electrochemical properties of LST, LSBT and LSFCr coatings with additions of carbon black pore former were investigated.
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OTU.1807/42429 |
| Date | 15 November 2013 |
| Creators | Zarzalejo, Maria |
| Contributors | Kesler, Olivera |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | en_ca |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0014 seconds