Orientadores: Paulo Roberto Mei, Marcelo Martins / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-16T16:54:20Z (GMT). No. of bitstreams: 1
Ritoni_Edson_M.pdf: 17028449 bytes, checksum: ff3c80af25659fb887c45f05f84c0a74 (MD5)
Previous issue date: 2010 / Resumo: Os aços inoxidáveis duplex são assim designados por apresentarem duas fases em sua microestrutura; a ferrita e a austenita. Para estudo foram selecionados dois aços inoxidáveis fundidos de acordo com as normas ASTM A890/A890M Gr. 1A (CD4MCu) e ASTM A890/890M Gr. 1B (CD4MCuN). O que difere estes dois aços inoxidáveis duplex é a presença do nitrogênio na composição química do CD4MCuN. O nitrogênio é um elemento fortemente austenitizante, o que favorece a formação desta fase neste aço, e faz com que as porcentagens das fases fiquem balanceadas em, aproximadamente, 50%. No aço inoxidável duplex que não contém nitrogênio há um desbalanceamento a favor da ferrita, que pode atingir valores em torno de 70% e como a austenita é responsável pela tenacidade neste aço, o mesmo não apresenta bons resultados nos ensaios de impacto. Um fator que pode favorecer o aumento de fase ferrita na microestrutura final é a temperatura de solubilização que, quanto mais elevada, maior será a fração volumétrica de ferrita. Com o interesse de avaliar a influência da temperatura de solubilização sobre a fração volumétrica das fases, foram realizados tratamentos térmicos de solubilização em temperaturas de 1050, 1100 e 1150 ºC por 2 horas, seguido de resfriamento em água. Para medir e comparar as propriedades mecânicas entre os dois aços foram realizados ensaios de impacto Charpy na condição solubilizado a 1100 ºC, em temperaturas de -195 a +120 ºC variando de 20 em 20 ºC e também ensaios de tração à temperatura ambiente. Na matriz ferrítica da microestrutura bruta de fundição destes aços, foram observados muitos precipitados ricos em cobre, caracterizados como Cu3N e Cu3,8Ni através de microscopia eletrônica de transmissão. A fração volumétrica de ferrita, aumentou com o aumento da temperatura de solubilização para os dois aços, porém a variação foi maior para o aço sem nitrogênio. O aço contendo nitrogênio apresentou maior energia média absorvida ao impacto (84J) e menor temperatura de transição dúctil para frágil (-70 ºC) quando comparado com 73 J e -35 ºC apresentados pelo aço sem nitrogênio, levando em consideração que o critério adotado foi o da energia média. Além disso, maior limite de resistência e alongamento apresentou o aço nitrogenado nos ensaios de tração. Com base nestes resultados, fica evidenciado o aumento na tenacidade destes aços proporcionado pela presença do nitrogênio. / Abstract: The duplex stainless steel has this name due the two different phases found in its microstructure; ferrite and austenite. To develop this research was selected two similar duplex steel, with and without nitrogen. One of then is the ASTM A890/A890M Gr. 1A (CD4MCu) and the other is the ASTM A890/890M Gr. 1B (CD4MCuN). Nitrogen is a strong austenitizing element witch favors the formation of this phase in this type of steel and allows the phase balance by, approximately, 50%. Duplex stainless steel that don't has nitrogen presents an unbalance between ferrite and austenite, favoring the ferrite formation that can reach values around 70% that makes the steel brittler and with lower toughness properties related to the same steel with nitrogen addition. One factor that may increase the ferrite phase in the final microstructure is the temperature of the solubilization; as higher it is, higher is the ferrite percentage. In the interest of measure influence of the solubilization temperature, solution heat treatments were performed at temperatures of 1050, 1100 and 1150 ºC during 2 hours, followed by water cooling. To measure and compare the toughness between both duplex stainless steel, with and without nitrogen, Charpy impact test was performed in the solubilized condition at 1100
ºC, with test temperature ranging from -195 to +120 ºC, in steps of 20 ºC. In the ferrite matrix of the microstructure as cast, were observed many precipitated rich in cooper, identified as Cu3N e Cu3,8Ni by transmission electronic microscopy. The ferrite content increased with solubilization temperature increase for both steel, however the variation was higher to the nitrogened steel. The nitrogened steel showed bigger energy absorbed in the impact (84 J) and smaller transition temperature of ductile to brittle fracture (-70 ºC), when compared with 73 J and 35 ºC showed for the steel without nitrogen. Moreover, higher tensile strength and elongation showed the nitrogened steel on tensile test. Based on these results, it is evident the increase in toughness of these steels provided by the presence of nitrogen. / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263127 |
Date | 16 August 2018 |
Creators | Ritoni, Edson |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Martins, Marcelo, Mei, Paulo Roberto, 1953-, Ferreira, Itamar, Casteletti, Luiz Carlos |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 95 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds