Barium Strontium Titanate (BST) was deposited on Pt/ZrO2 / SiO2/Si substrates using liquid source metal organic chemical vapor deposition. A stoichiometry series was deposited with various GrII/Ti ratios (0.658 to 1.022) and a temperature series was deposited at 550 to 700°C. The thin films were characterized using transmission electron microscopy.
Both series of samples contained cubic perovskite BST and an amorphous phase. The grain size increased and the volume fraction of amorphous phase decreased with increasing deposition temperature. The electrical and microstructural properties improved as the GrII/Ti ratio approached 1 and deteriorated beyond 1. This research demonstrates that BST thin films are a strong candidate for future
MOS transistor gate insulator applications.
Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc279410 |
Date | 05 1900 |
Creators | Pena, Piedad |
Contributors | Pinizzotto, Russell F., Marshall, James L., 1940- |
Publisher | University of North Texas |
Source Sets | University of North Texas |
Language | English |
Detected Language | English |
Type | Thesis or Dissertation |
Format | ix, 89 leaves : ill., Text |
Rights | Public, Copyright, Copyright is held by the author, unless otherwise noted. All rights reserved., Pena, Piedad |
Page generated in 0.0129 seconds