Previous issue date: 2015-07-22 / FACEPE / O íon borohidreto, BH
4 , é um redutor de íons metálicos que tem sido usado extensivamente
para a formação de partículas metálicas. Neste trabalho, depositamos
nanopartículas de Fe, Ni e Co em vidro poroso, o Vycor. O Vycor é um vidro poroso,
com poros de diâmetro entre 4 e 20 nm, sendo quimicamente inerte, composto basicamente
de SiO2, 96% do material, possuindo espaços vazios de 28% do volume e
uma área super cial interna de 250 m2=g. A reação para inserção das nanoparticulas
magnéticas nos poros do material é feita mergulhando-o nas soluções reagentes. A
reação ocorre no interior dos poros, produzindo então as nanopartículas.
As medidas de magnetização são realizadas num VSM (Vibrating Sample Magnetometer)
modelo EV7 Microsense, com uma sensibilidade de 106emu. Em todas
as amostras pudemos observar os efeitos do controle de tamanho, uma vez que foram
comparados os resultados do material sintetizado fora do con namento. Para o Fe
e Ni, que têm diâmetros críticos maiores, foi possível observar um comportamento
superparamagnético. A observação desse comportamento é corroborada tanto pelas
medidas de ZFC - FC quanto por medidas de histerese a temperaturas mais altas.
Através do comportamento de Hc em função da temperatura foi possível estimar o
tamanho médio das partículas. Os resultados estão em acordo com as medidas encontradas nas curvas de ZFC-FC. Os estudos das interações das partículas, através
do plot de Henkel, mostraram que a interação entre a nanopartículas é predominantemente
dipolar.
Foi evidenciado que por este método se pode ter um controle sobre tamanho das
partículas magnéticas através de reações químicas no interior dos poros. Sendo uma
rota promissora para síntese e estudo de outros materiais de dimensões nanométricas. / The ion borohydride, BH
4 , a reducing metal ion that has been used extensively
for the formation of metal particles. In this work, we deposited nanoparticles of Fe,
Ni and Co in porous glass, Vycor. The Vycor is a porous glass with pore diameters
between 4 and 20 nm, being chemically inert, essentially consisting of SiO2, 96%
material having voids 28% volume and an internal surface area of 250 m2=g. The
reaction for insertion of magnetic nanoparticles in the pores of the material is made
by immersing it in the reagent solutions. The reaction occurs within the pores, thus
producing nanoparticles.
Magnetization measurements are performed in a VSM (Vibrating Sample Magnetometer)
model EV7 Microsense, with a sensitivity of 106emu. In all the samples we
could observe the e ects control of size, as compared to the results of the synthesized
material outside the containment. For Fe and Ni, which have larger critical diameters,
it was possible to observe a superparamagnetic behavior. The observation of
this behavior is supported by both measures ZFC - FC as hysteresis measurements at
higher temperatures. Through the behavior Hc depending on the temperature it was
possible to estimate the average particle size. The results are in agreement with the
measurements of ZFC-FC. The studies of particle interaction, by Henkel plot showed
that the interaction between the nanoparticles is predominantly dipole.
It was shown that by this method one can have reasonable control over the size
of the magnetic particles by chemical reactions within the pores. It is a promising
route to synthesis and study of other materials nanometrics dimensions.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/16766 |
Date | 22 July 2015 |
Creators | CAVALCANTI, Paulo José Fonseca |
Contributors | RODRIGUES, Alexandre Ricalde |
Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Fisica, UFPE, Brasil |
Source Sets | IBICT Brazilian ETDs |
Language | Breton |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds