Philosophiae Doctor - PhD / Carbon dioxide emissions have become a major concern as they are one of the contributing factors to the “green-house” effect. Recently, much effort has been put into separating carbon dioxide (CO2) from flue gases linked to the combustion processes at fixed point sources. The development of solid sorbents for adsorption based on CO2 capture has attracted much attention. Ordered Mesoporous Silica (OMS) materials have recently attracted much attention as solid adsorbents for capturing CO2. OMS have been investigated for this purpose owing to their high pore volume, large surface area and ease of functionalizationIn this work we report on the synthesis of OMS viz. MCM-41 and SBA-15 along with amorphous silica as adsorbents for CO2 capture. MCM-41 was prepared with surfactants having different alkyl chain lengths (C14TABr, C16TABr and C18TABr) where TABr is trimethylammonium bromide. SBA-15 was prepared using a Triblock copolymer as a structure directing agent for the organization of polymerizing silica species. Commercial amorphous silica gel was used for comparative purposes. Initial characterization OMS with powder X-Ray diffraction (XRD) and small angle diffraction (SAXS) yielded diffraction patterns which may be associated with well-ordered structures of hexagonal mesoporous material. Ease of preparation for MCM-41 materials allowed for convenient scale- up, obtaining highly ordered mesoporous silica MCM-41 at room temperature. SBA-15 was also found to be scaled up with considerable ease through increasing the volume of the autoclave during hydrothermal treatment. Structural, morphological and textural properties of the adsorbents were characterized by N2 physisorption measurements, Transmission Electron Microscopy (TEM), Scanning Electron Microscopy (SEM) and Thermogravimetric Analysis (TGA). TEM confirmed the hexagonal structure; SEM showed that C14MCM-41 had spheroidal particle morphology whereas SBA-15 displayed rod-like structures. High surface areas of up to 1302, 1186, 1211 and 1024 m2/g for C14MCM-41, C16MCM-41, C18MCM-41 and SBA-15, respectively were obtained. The pore size of MCM-41 materials was increased from 2.6 nm for C14MCM-41 to 4.4 nm in diameter for C18MCM-41 using surfactants with different alkyl chain lengths. CO2 adsorption characteristics of OMS were studied using CO2-temperature programmed desorption (TPD). The results showed that C14MCM-41, C16MCM- 41, C18MCM-41 and SBA-15 desorbed 0.19, 0.16, 0.11 and 0.26 mmol/g respectively. The synthesized OMS were then further modified by grafting various amine moieties on their surfaces in order to increase their CO2 adsorptive capabilities. 3-(Aminopropyl)triethoxysilane (APS), N-[3-(trimethoxysilyl)propyl]ethylene- diamine (TPED), 3-chloropropyl)-trimethoxysilane (CPS), ethyl 2-bromopropanoate, tris(2-aminoethyl)amine (TREN) and guanidine. Several characterization techniques such as XRD, SAXS, HRTEM, HRSEM, TGA, Fourier Transform Infra-Red (FT-IR) spectroscopy, CO2 isotherms and CO2-TPD were used to analyze amine grafted solid sorbents for CO2 capture. The results revealed that the structural integrity of the amine modified sorbents was not compromised during the grafting process. The structural properties of the supports, such as surface area and pore size, nature of amine and the number of amine groups, affected the loading and CO2 adsorption capacity of chemically grafted sorbents. APS grafted amorphous silica gel adsorbed 0.67 mmol/g CO2, which proved to be the highest compared to C18MCM-41 and SBA-15 grafted with APS and TPED. C18MCM-41, SBA-15 and amorphous silica gel were also grafted with TREN and adsorbed 0.42, 0.51 and 0.27 mmol/g of CO2, respectively. A systematic study of guanidine grafted on C14MCM-41, C16MCM-41 and C18MCM-41 was investigated, for the first time, to the best of our knowledge. Structural properties like variation in pore size, proved to enhance the adsorption capacity of the adsorbent, coupled with the guanidine molecules grafted on MCM-41 materials. C18MCM-41-guanidine showed the highest CO2 uptake of the guanidine grafted MCM-41 materials, adsorbing 0.30 mmol/g. A novel synthetic route to TPED-TREN grafted C18MCM-41 and SBA-15, using ethyl 2-bromopropanoate as a linker, was investigated as a potential adsorbent for CO2 capture, for the first time. C18MCM-41-TPED-TREN and SBA-15-TPED-TREN CO2 adsorption capacity were found to be 0.14 and 0.14 mmol/g, respectively.
Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:uwc/oai:etd.uwc.ac.za:11394/4464 |
Date | January 2014 |
Creators | Piet, Marvin |
Contributors | Titinchi, Salam, Abbo, Hanna |
Publisher | University of the Western Cape |
Source Sets | South African National ETD Portal |
Language | English |
Detected Language | English |
Rights | University of the Western Cape |
Page generated in 0.0014 seconds