The thermal stability of p-type CdTe crystals by using conductivity and Hall-effect measurements have been studied at room and slightly increased temperatures. It was observed that thermal changes often implicate an anomalous behavior of the hole density characterized by reversible decrease/increase in a heating/cooling regime. This anomaly was explained by a transfer of fast diffusing donors between Te inclusions and the bulk of the sample. Sodium and potassium were determined by the Secondary Ion Mass Spectroscopy (SIMS) as the most probable diffusing species. To verify this behavior samples were also treated in saturated NaCl solution for different time intervals in order to examine the influence of the oxide layer and sodium on the surface of the sample. To determine the structure of the surface the sample was characterized by ellipsometric and X-ray photoelectron spectroscopy (XPS) and SIMS. Very low determined diffusion coefficient of Na was explained by trapping of Na in Cd sublattice
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:404554 |
Date | January 2019 |
Creators | Korcsmáros, Gabriel |
Contributors | Moravec, Pavel, Šikula, Josef, Toušková, Jana |
Source Sets | Czech ETDs |
Language | English |
Detected Language | English |
Type | info:eu-repo/semantics/doctoralThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.1291 seconds