A novel electrically conducting polymer, poly(2-dodecyl-4,7-di(selenophen-2-yl)benzotriazole) (Poly(SBT)), containing selenophene as a strong donor and benzotriazole as a strong acceptor group was synthesized by electrochemical polymerization. Homopolymerization and copolymerization ( in the presence of 3,4-ethylenedioxythiophene (EDOT) ) was achieved in acetonitrile/ dichloromethane(95/5 v/v) with 0.1M tetrabutylammonium hexafluorophosphate (TBAPF6). The electrochemical and optical properties of homopolymer and copolymer were investigated by Cyclic voltammetry, UV-Vis, near IR Spectroscopy. Cyclic voltammetry and spectroelectrochemistry studies demonstrated that homopolymer can be reversibly reduced and oxidized (both n- and p-doped) between -1.9 V and 1.4 V, at a scan rate of 100 mV/s. Optical contrast was calculated as 32% and 56% with a switching time of 2.4 s and 0.4 s at 511 and 1200 nm respectively. Poly(SBT) exhibits a & / #955 / max value of 511nm and a band gap of 1.67eV.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/3/12609595/index.pdf |
| Date | 01 September 2005 |
| Creators | Ardahan, Gulben |
| Contributors | Toppare, Levent |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.002 seconds