The first objective of this thesis was to determine the effect of using self-consolidating concrete versus normal concrete on transfer and development lengths, and flexural strengths of prestressed members. Three small rectangular members were made, two cast with SCC mixes and one cast with a conventional mix, to determine the transfer length of each mix. Transfer lengths of both ends of each member were determined by measuring the concrete surface strains. The change in the transfer length was monitored by determining the transfer length of each member at prestress release, 7 days after release, and 28 days after release. All concrete mixes had lower than code determined transfer lengths at prestress release. Each concrete mix showed between a 12 to 56 percent increase in transfer length after 28 days. One SCC mix exceeded the ACI code stipulated 50 strand diameters 7 days after prestress transfer. The other SCC mix was consistently below the transfer length of the conventional concrete.
Separate development length members were cast in a stay-in-place steel form used for creating structural double tees. Each development length member was a stub tee. Iterative load testing was performed to determine the development length of each SCC and conventional mix. Development lengths for both SCC mixes were approximately 20 percent shorter than ACI and AASHTO code predictions. A development length for the conventional concrete was not determined due to non-repeating test data. The flexural strength of each member was determined during load testing. All concrete mixes achieved higher than the ACI predicted strengths.
The second objective of this thesis was to experimentally measure prestress losses and compare these experimental values to theoretical models. Crack initiation and crack reopening tests were performed to experimentally determine the prestress losses in each member. Three theoretical models were evaluated, the sixth edition PCI Design Handbook suggested model, a 1975 PCI Committee on Prestress Losses model, and the AASHTO LRFD prestress loss model. The crack initiation experimental values tended to be between 10 and 15 percent lower than theoretical models. In general, the crack reopening prediction of the effective prestress had a good correlation with theoretical models. This suggests crack reopening tests can be used as predictors of effective prestress, and as such, predictors of prestress losses in future experimental research. Additionally, the concrete type was shown to affect the prestress losses determined in the development length members. The SCC members tended to have higher effective prestress forces than the conventional concrete members, and thus had less prestress losses due to creep and shrinkage than the conventional concrete members. / Master of Science
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/33161 |
| Date | 04 June 2007 |
| Creators | Trent, Justin David |
| Contributors | Civil Engineering, Wang, Linbing, Roberts-Wollmann, Carin L., Cousins, Thomas E. |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Detected Language | English |
| Type | Thesis |
| Format | application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | JTrentThesis.pdf |
Page generated in 0.0022 seconds