abstract: Perovskite solar cells are the next generation organic-inorganic hybrid technology and have achieved remarkable efficiencies comparable to Si-based conventional solar cells. Since their inception in 2009 with an efficiency of 3.9%, they have improved tremendously over the past decade and recently demonstrated 25.2% efficiency for single-junction devices. There are a few hurdles, however, that prevent this technology from realizing their full potential, such as stability and toxicity of the perovskites. Apart from solution processing in the fabrication of perovskites, precursor composition plays a major role in determining the quality of the thin film and its general properties. This work studies novel approaches for improving the efficiency and stability of the perovskite solar cells with minimized toxicity. The effect of excess Pb on photo-degradation in MAPbI3 perovskites in an inverted device architecture was studied with a focus on improving stability and efficiency. Precursor concentration with 5% excess Pb was found to be optimal for better efficiency and stability against photo-degradation. Further improvements in efficiency were made possible through the addition of Zirconium Acetylacetonate as a secondary electron buffer layer. A concentration of 1.5mg/ml was found to be optimal for demonstrating better efficiency and stability. Partial substitution of Pb with non-toxic Sr was also studied for improving the stability of inverted devices. Using acetate-derived precursors, 10% Sr was introduced into perovskites for improvements to the stability of the device.
In another study, triple-cation perovskites with FAMACs cations were studied with doping different amounts of Phenyl Ethyl Ammonium (PEA) to induce a quasi 2D-3D structure for improved moisture stability. Doping the perovskite with 1.67% PEA was found to be best for improved morphology with fewer pinholes, which further resulted in better VOC and stability. A passivation effect for triple-cation perovskites was further proposed with the addition of a Guanidinium Iodide layer on the perovskite. Concentrations of 1mg/ml and 2mg/ml were demonstrated to be best for reducing defects and trap states and increasing the overall stability of the device. / Dissertation/Thesis / Doctoral Dissertation Materials Science and Engineering 2020
| Identifer | oai:union.ndltd.org:asu.edu/item:62909 |
| Date | January 2020 |
| Contributors | Yerramilli, Aditya (Author), Alford, Terry (Advisor), Theodore, David (Committee member), Chen, Yuanqing (Committee member), Arizona State University (Publisher) |
| Source Sets | Arizona State University |
| Language | English |
| Detected Language | English |
| Type | Doctoral Dissertation |
| Format | 156 pages |
| Rights | http://rightsstatements.org/vocab/InC/1.0/ |
Page generated in 0.0022 seconds