Previous issue date: 2015-12-18 / Esse trabalho teve como objetivo, avaliar a influência do tipo de precursor, fonte de íons de ferro, e sua concentração na dopagem do sistema Zn1-xFexO de modo a se obter um produto com ferrimagnetismo a temperatura ambiente para uso como semicondutor magnético diluído. Para esse fim, inicialmente avaliou-se a influência do tipo de precursor (nitrato de ferro III, sulfato de ferro II e acetato de ferro II) sobre a estrutura, morfologia, propriedades térmicas e magnéticas do sistema Zn1-xFexO com concentração de íons de Fe2+ e Fe3+ de 0,4 mol. Posteriormente avaliou-se o efeito da concentração de íons de ferro III variando de 0,05 a 0,4 mol sobre a estrutura e magnetismo do sistema Zn1- xFexO. Durante as reações para obtenção do produto foram feitas medições de temperatura e do tempo de reação. As amostras foram caracterizadas por: difração de raios X, análise química por fluorescência de raios X por energia dispersiva, microscopia eletrônica de varredura com mapeamento por EDS, distribuição granulométrica, análise por adsorção de nitrogênio, magnetometria de amostra vibrante e análise termogravimétrica. Os resultados mostraram que o tipo de precursor influenciou diretamente na estrutura, morfologia e magnetismos das amostras, sendo o precursor nitrato de ferro III o que possibilitou à formação de um material ferrimagnético a temperatura ambiente. Para as amostras dopadas, os espectros de DRX mostraram que até a concentração de 0,20 mol de íons ferro III resultou num sistema monofásico com comportamento ferrimagnético à temperatura ambiente, o que caracterizou a formação de um semicondutor magnético diluído. Para demais concentrações foi observado traços da fase FeFe2O4 e que às interações de troca entre os íons Fe - Fe e possivelmente o aumento da concentração de vacância de oxigênio na rede do ZnO suprimiu o comportamento ferrimagnético pela competição do comportamento ferrimagnético/paramagnético. Portanto, pode-se concluir que o precursor nitrato de ferro III com concentração de até 0,20 mol foi a melhor condição para obtenção de produto com característica para uso como semicondutor magnético diluído usando a técnica de síntese por reação de combustão. / The objective of this study is to evaluate the influence the type of precursor, source of iron ions, and its concentration in the doping Zn1-xFexO system in order to obtain a product with ferromagnetism at room temperature for use as magnetic semiconductor diluted. For this purpose, it was firstly evaluated the influence of the type of precursor (iron III nitrate, iron sulfate II, iron acetate II) on the structure, morphology, thermal and magnetic properties of Zn1-xFexO system concentration of Fe2+ and Fe3+ ions of 0.4 mol. After that, it was evaluated the effect of concentration of iron III ions ranging from 0.05 to 0.4 mol on the structure and magnetism of Zn1-xFexO system. During the reactions, there were made measurements of temperature and time. The samples were characterized by: X-ray diffraction, chemical analysis by fluorescence X-ray energy dispersive, scanning electron microscopy, with mapping by EDS, particle size analysis, analysis by nitrogen adsorption, vibrating sample magnetometer and thermal gravimetric analysis. The results have shown that the type of precursor influenced directly the structure, morphology and magnetism of the samples and the precursor of iron nitrate III was the one which favored the obtention of the ferromagnetism material monophasic at room temperature. For the doped samples, the XRD spectra showed that the concentrations until 0.20 mol of iron III ions resulted in a monophasic system with ferromagnetic behavior at room temperature, which characterized the formation of a diluted magnetic semiconductor. For the other concentrations, it was observed traces of MnFe2O4 phase and that the exchange interactions between the ionsFe - Fe and possibly the increasing of oxygen vacancy concentration in ZnO network suppressed the ferromagnetic behavior by the competition of ferromagnetic / paramagnetic one. Therefore, it can be concluded that the precursor of iron III nitrate concentration to 0.20 mol was the best condition for obtaining a product with characteristics for use as a dilute magnetic semiconductor using the synthetic technique by combustion.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1038 |
| Date | 25 June 2018 |
| Creators | MACHADO, Lucius Vinicius Rocha. |
| Contributors | COSTA, Ana Cristina Figueiredo de Melo., SILVA, Manoel Ribeiro da., SILVA, Manoel Ribeiro da., CORREA, Ronaldo Ribeiro., TORQUATO, Ramon Alves., VIEIRA, Lucianna da Gama Fernandes., VIEIRA, Débora Albuquerque. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | PROQALIS/IFMA |
Page generated in 0.0028 seconds