This thesis describes a simple method for the separation of strontium from an excess of barium using ion exchange techniques. This process has been applied to the separation of strontium and rubidium in barites. The resin used is Dowex-50 (200-400 mesh, hydrogen form) and the column dimensions are 1.1 by 8 cm. The column is eluted at room temperature with 1.5 M hydrochloric acid at a flow rate of approximately 1 ml/ min. Strontium and rubidium from two samples of barites were analysed using a solid-source mass spectrometer to determine strontium-87/strontium-86 ratios.
The above chemical techniques have also been employed in the separation of strontium and rubidium from galenas. The concentration of strontium in one sample of galena (U.B.C. No. 1) has been determined using isotope dilution techniques. The results show an absence of strontium in the galena sample studied.
Finally the common strontium ratios of two barite samples are compared with common lead ratios of associated galenas (Slawson and Austin, 1962) and a possible correlation between these ratios has been observed. / Science, Faculty of / Earth, Ocean and Atmospheric Sciences, Department of / Graduate
Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/36303 |
Date | January 1967 |
Creators | Kalra, Ashok Kumar |
Publisher | University of British Columbia |
Source Sets | University of British Columbia |
Language | English |
Detected Language | English |
Type | Text, Thesis/Dissertation |
Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0017 seconds