This in vitro study evaluated the bond and compression strength of cemented leucite reinforced glass ceramics in bovine tooth enamel, comparing three etching times with hydrofluoric acid 10% of the ceramic surface (20, 60 and 90 seconds) and two adhesive treatments (adhesive system + silane and universal adhesive system). For the bond strength test, 120 ceramic cylinders (2mm diameter x 2mm length; n=20) were etched and cemented (80m thick) in enamel with a dual resin cement, varying the adhesive treatment, obtaining the groups: UEXC20s, UEXC60s, UEXC90s, USBU20s, USBU60s, USBU90s. After 24 hours, the shear bond strength test was performed on a universal test machine (0.5mm/min, 50kgf). For the compression test, 30 ceramic plates (5x5mm with 1mm thick, n=5) were etched, received the same adhesive treatments and were cemented (80m) in enamel, obtaining the following groups: CEXC20s, CEXC60s, CEXC90s, CSBU20s, CSBU60s, CSBU90s. After 24 hours of cementation, the compression test (0.5mm/min, 500kgf) was performed. Statistical analysis was performed using two-way ANOVA and Tukey test (=.05). For the shear bond strength test significant differences were found among the adhesives (p<.05). For the etching times there were no differences (p=.059). However, there was a significant interaction between the adhesives and the etching times (p=.021). At 60 seconds, the Silane + ExciTE F DSC Adhesive presented the highest bond strength values (47.53±16.70Mpa). And at 20 seconds, the Universal adhesive presented the lowest bond strength values (27.72±10.76Mpa). For the compression test there were no significant differences between the adhesives (p=.571) and between the times (p=.154). The group that presented the highest values of compression force was the Universal adhesive at 60 seconds (1757.89±200.47N). The lowest values were also the Universal adhesive, but at 90 seconds (1213.30±546.34N). The study concluded that the silane associated with the ExciTE F DSC adhesive showed the highest bond strength values at the etching time of 60 seconds with 10% hydrofluoric acid, without compromising the compressive strength of the leucite reinforced ceramic. / Este estudo in vitro avaliou a resistência de união e compressão da cerâmica reforçada por cimentada em esmalte de dentes bovinos, comparando-se três tempos de condicionamento com ácido fluorídrico 10% da superfície cerâmica (20, 60 e 90 segundos) e dois tratamentos adesivos (sistema adesivo + silano e sistema adesivo universal). Para o teste de resistência de união (U), 120 cilindros cerâmicos (2mm diâmetro x 2mm comprimento; n=20) foram condicionados e cimentados (80 m de espessura) em esmalte, com cimento resinoso dual, variando-se o tratamento adesivo, obtendo-se os grupos: UEXC20s, UEXC60s, UEXC90s, USBU20s, USBU60s, USBU90s. Após 24h, foi realizado o teste de cisalhamento (0,5mm/min, 50kgf). Para o teste de compressão (C), 30 placas cerâmicas (5x5mm com 1mm de espessura; n=5) foram condicionadas, receberam os mesmos tratamentos adesivos e foram cimentadas (80m) em esmalte, obtendo-se os grupos: CEXC20s, CEXC60s, CEXC90s, CSBU20s, CSBU60s, CSBU90s. Após 24h da cimentação, foi realizado o teste de compressão (0,5mm/min, 500kgf). Foi realizada a análise estatística por meio de ANOVA dois critérios e teste de Tukey (P < 0,05). Para o teste de cisalhamento diferenças significativas foram encontradas entre os adesivos (p<0,05). Para os tempos de condicionamento não houve diferenças significativas (p=0,059). No entanto, houve interação significativa entre os adesivos e os tempos de condicionamento (p=0,021). No tempo de 60 segundos, o silano + adesivo ExciTE F DSC apresentou os maiores valores de resistência de união (47,53±16,70Mpa). E no tempo de 20 segundos, o adesivo Universal apresentou os menores valores de resistência de união (27,72±10,76Mpa). Para o teste de compressão não houve diferenças significativas entre os adesivos (p=0,571) e entre os tempos (p=0,154). O grupo que apresentou maiores valores de força de compressão foi o adesivo Universal no tempo de 60 segundos (1757,89±200,47N). Já os menores valores, foi também o adesivo Universal, mas no tempo de 90 segundos (1213,30±546,34N). Pode-se concluir que, o Silano associado ao adesivo ExciTE F DSC, mostrou os maiores valores de resistência de união no tempo de condicionamento de 60 segundos com ácido fluorídrico a 10%, sem comprometer a resistência a compressão da cerâmica reforçada por leucita.
| Identifer | oai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-05092019-205033 |
| Date | 11 March 2019 |
| Creators | Libardi, Camila Cruz |
| Contributors | Bombonatti, Juliana Fraga Soares |
| Publisher | Biblioteca Digitais de Teses e Dissertações da USP |
| Source Sets | Universidade de São Paulo |
| Language | English |
| Detected Language | English |
| Type | Dissertação de Mestrado |
| Format | application/pdf |
| Rights | Liberar o conteúdo para acesso público. |
Page generated in 0.0023 seconds